Synthesis and effect of hyperbranched (3-hydroxyphenyl) phosphate as a curing agent on the thermal and combustion behaviours of novolac epoxy resin

被引:38
作者
Deng, J [1 ]
Shi, WF [1 ]
机构
[1] Univ Sci & Technol China, State Key Lab Fire Sci, Dept Polymer Sci & Engn, Hefei 230026, Anhui, Peoples R China
基金
中国国家自然科学基金;
关键词
epoxy resin; hyperbranched polymer; phosphorus; flame retardancy; thermal property; combustion behaviour;
D O I
10.1016/j.eurpolymj.2003.12.015
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
A novel type of hyperbranched (3-hydroxyphenyl) phosphate (HHPP) with high functionality as a curing agent of epoxy resins was synthesized and characterized by FTIR, H-1 NMR and vapor phase osmometry (VPO). The cured epoxy resin with HHPP possessed improved glass transition temperature. The thermostability and flame retardancy of O-cresol novolac epoxy resin cured with different contents of HHPP were investigated by thermogravimetric analysis (TGA), limiting oxygen index (LOI) and cone calorimetry. The obtained results show that the samples containing a higher percentage of HHPP exhibit relatively lower thermostability at lower temperature while higher thermostability at elevated temperature and more char was formed compared with those containing a lower percentage of HHPP. The LOI value increased from 22.0 to 30.0 when HHPP, instead of 1,3-dihydroxybenzene, was used as a curing agent. The 25 wt% addition of HHPP in the curing agent complex effectively decreased the heat release rate and improved the char yield to the content nearly similar as those of the epoxy resin cured with pure HHPP. (C) 2003 Elsevier Ltd. All rights reserved.
引用
收藏
页码:1137 / 1143
页数:7
相关论文
共 29 条
[1]  
Chen-Yang YW, 2000, J POLYM SCI POL CHEM, V38, P972, DOI 10.1002/(SICI)1099-0518(20000315)38:6<972::AID-POLA6>3.0.CO
[2]  
2-N
[3]   A cone calorimeter test for the measurement of flammability properties of insulated wire [J].
Elliot, PJ ;
Whiteley, RH .
POLYMER DEGRADATION AND STABILITY, 1999, 64 (03) :577-584
[4]  
Ellzey KA, 2003, POLYM BULL, V50, P235
[5]   An A2+B3 approach to hyperbranched aliphatic polyethers containing chain end epoxy substituents [J].
Emrick, T ;
Chang, HT ;
Fréchet, JMJ .
MACROMOLECULES, 1999, 32 (19) :6380-6382
[6]  
Grand A., 2000, FIRE RETARDANCY POLY, P147
[7]   FLAME-RETARDANT MODIFICATION OF UV-CURABLE RESINS WITH MONOMERS CONTAINING BROMINE AND PHOSPHORUS [J].
GUO, WJ .
JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY, 1992, 30 (05) :819-827
[8]  
Hsiue GH, 2001, J APPL POLYM SCI, V79, P342, DOI 10.1002/1097-4628(20010110)79:2<342::AID-APP180>3.0.CO
[9]  
2-8
[10]  
Jeng RJ, 2001, J APPL POLYM SCI, V82, P3526