Hydrogen embrittlement susceptibility of over aged 7010 Al-alloy

被引：56

作者：

Kannan, M. Bobby ^{[1
]}

Raja, V. S. ^{[1
]}

机构：

[1] Indian Inst Technol, Bombay 400076, Maharashtra, India

来源：

JOURNAL OF MATERIALS SCIENCE | 2006年 / 41卷 / 17期

关键词：

D O I：

10.1007/s10853-006-0287-1

中图分类号：

T [工业技术];

学科分类号：

08 [工学];

摘要：

Slow strain rate testing (SSRT) was carried out on over aged 7010 Al-alloy in laboratory air, glycerin and 3.5 wt.% NaCl solution with and without cathodic charging to study the hydrogen embrittlement susceptibility of the alloy in over aged condition. It was found that the over aged alloy exhibited high resistance to stress corrosion cracking (SCC) than hydrogen embrittlement (HE). The high SCC resistance is due to the modification in the grain boundary precipitate morphology and chemistry due to over aging, however it is suggested that the dislocations in the alloy are not completed annealed during over aging to arrest HE.

引用

页码：5495 / 5499

页数：5

共 16 条

[1]

EVIDENCE FOR DISLOCATION TRANSPORT OF HYDROGEN IN ALUMINUM [J].

ALBRECHT, J ;

BERNSTEIN, IM ;

THOMPSON, AW .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1982, 13 (05) :811-820

[2]

ROLE OF MICROSTRUCTURE IN HYDROGEN-ASSISTED FRACTURE OF 7075 ALUMINUM [J].

ALBRECHT, J ;

THOMPSON, AW ;

BERNSTEIN, IM .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1979, 10 (11) :1759-1766

[3]

HAAS M, 2002, THESIS U GRONINGEN G, P96

[4]

THE EFFECT OF COPPER CONTENT AND MICROSTRUCTURE ON THE HYDROGEN EMBRITTLEMENT OF AL-6ZN-2MG ALLOYS [J].

HARDWICK, DA ;

THOMPSON, AW ;

BERNSTEIN, IM .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1983, 14 (12) :2517-2526

[5]

Kannan M.B., 2003, CORROSION-US, V59, P881

[6]

Determination of true stress corrosion cracking susceptibility index of a high strength Al alloy using glycerin as the non-corrosive atmosphere [J].

Kannan, MB ;

Raja, VS ;

Mukhopadhyay, AK .

SCRIPTA MATERIALIA, 2004, 51 (11) :1075-1079

[7]

KLIMOWICZ TF, 1978, METALL TRANS A, V9, P597, DOI 10.1007/BF02646418

[8]

MUKHOPADHYAY AK, 2001, JT STAL HON S AI ALL, P63

[9]

MICROSTRUCTURAL EFFECTS ON HYDROGEN EMBRITTLEMENT IN A HIGH-PURITY 7075-ALUMINUM ALLOY [J].

NGUYEN, D ;

THOMPSON, AW ;

BERNSTEIN, IM .

ACTA METALLURGICA, 1987, 35 (10) :2417-2425

[10]

ON THE NATURE OF THE OCCLUDED CELL IN THE STRESS-CORROSION CRACKING OF AA-7075-T651 - EFFECT OF POTENTIAL, COMPOSITION, MORPHOLOGY [J].

NGUYEN, TH ;

BROWN, BF ;

FOLEY, RT .

CORROSION, 1982, 38 (06) :319-326

← 1 2 →