Anode Supported Solid Oxide Fuel Cells - Deconvolution of Degradation into Cathode and Anode Contributions

被引：9

作者：

Hagen, A. ^{[1
]}

Liu, Y. L. ^{[1
]}

Barfod, R.

Hendriksen, P. V. ^{[1
]}

机构：

[1] Riso Natl Lab, Fuel Cells & Solid State Chem Dept, DK-4000 Roskilde, Denmark

来源：

SOLID OXIDE FUEL CELLS 10 (SOFC-X), PTS 1 AND 2 | 2007年 / 7卷 / 01期

关键词：

D O I：

10.1149/1.2729105

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

The degradation of anode supported cells was studied over 1500 h as function of cell polarization either in air or oxygen on the cathode. Based on impedance analysis, contributions of anode and cathode to the increase of total resistance were assigned. Accordingly, the degradation rates of the cathode were strongly dependent on the pO(2); they were significantly smaller when testing in oxygen compared to air. Microstructural analysis of the cathode/electrolyte interface of a not-tested reference cell carried out after removal of the cathode showed sharp craters on the electrolyte surface where the LSM particles had been located. After testing in air, these craters flattened out and decreased in size, indicating the decrease of three phase boundary length. In contrast, they remained almost unchanged after testing in oxygen giving an explanation for the observed smaller - mainly anode related degradation rate.

引用

页码：301 / 309

页数：9

共 14 条

[1] Break down of losses in thin electrolyte SOFCs [J].

Barfod, R ;

Hagen, A ;

Ramousse, S ;

Hendriksen, PV ;

Mogensen, M .

FUEL CELLS, 2006, 6 (02) :141-145

[2]

BARFOD R, 2005, SOLID STATE ELECTRON, P121

[3]

BARFOD R, 2007, J ELECTROCH IN PRESS, V154

[4] Identification of O2 reduction processes at yttria stabilized zirconia|doped lanthanum manganite interface [J].

Chen, XJ ;

Khor, KA ;

Chan, SH .

JOURNAL OF POWER SOURCES, 2003, 123 (01) :17-25

[5] MICROSTRUCTURAL AND MICROCHEMICAL CHARACTERIZATION OF THE INTERFACE BETWEEN LA0.85SR0.15MNO3 AND Y2O3-STABILIZED ZRO2 [J].

CLAUSEN, C ;

BAGGER, C ;

BILDESORENSEN, JB ;

HORSEWELL, A .

SOLID STATE IONICS, 1994, 70 :59-64

[6] Properties and performance of SOFCs produced on a pre-pilot plant scale [J].

Hagen, A ;

Menon, M ;

Barfod, R ;

Hendriksen, PV ;

Ramousse, S ;

Larsen, PH .

FUEL CELLS, 2006, 6 (02) :146-150

[7] Degradation of anode supported SOFCs as a function of temperature and current load [J].

Hagen, A ;

Barfod, R ;

Hendriksen, PV ;

Liu, YL ;

Ramousse, S .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2006, 153 (06) :A1165-A1171

[8]

HENEKA MJ, 2005, SOLID STATE ELECTRON, P215

[9] Impedance of solid oxide fuel cell LSM/YSZ composite cathodes [J].

Jorgensen, MJ ;

Mogensen, M .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2001, 148 (05) :A433-A442

[10] INTERACTIONS BETWEEN A THICK-FILM LAMNO3 CATHODE AND YSZ SOFC ELECTROLYTE DURING HIGH-TEMPERATURE AGING [J].

KUSCER, D ;

HOLC, J ;

HROVAT, M ;

BERNIK, S ;

SAMARDZIJA, Z ;

KOLAR, D .

SOLID STATE IONICS, 1995, 78 (1-2) :79-85

← 1 2 →