Effect of Fe and Cr addition on the sintering behavior of ZrB2 produced by self-propagating high-temperature synthesis

被引：57

作者：

Mishra, SK ^{[1
]}

Das, SK ^{[1
]}

Ray, AK ^{[1
]}

Ramachandrarao, P ^{[1
]}

机构：

[1] Natl Met Lab, Jamshedpur 831007, Bihar, India

来源：

JOURNAL OF THE AMERICAN CERAMIC SOCIETY | 2002年 / 85卷 / 11期

关键词：

D O I：

10.1111/j.1151-2916.2002.tb00540.x

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

An investigation of the sintering behavior of ZrB2 powder with Fe and Cr (0 to 20 wt%) addition was conducted. It was observed that Fe addition helps to enhance the density of ZrB2 only up to 10 wt%. Further addition of Fe degrades the sintering by segregation of Fe-rich phases. Formation of a eutectic phase containing a Fe:Zr ratio of 92.57:7.43 was also found in Fe-added samples. The addition of Cr to a ZrB2 matrix was found to result in swelling of the samples, leading to several cracks.

引用

页码：2846 / 2848

页数：3

共 14 条

[1] Synthesis and analysis of ZrB2-based composites [J].