Over-etching effects on micro-tensile bond strength and failure patterns for two dentin bonding systems

被引:94
作者
Hashimoto, A
Ohno, H
Kaga, M
Sano, H
Tay, FR
Oguchi, H
Araki, Y
Kubota, M
机构
[1] Iwate Med Univ, Sch Dent, Dept Operat Dent & Endodont, Morioka, Iwate 0208505, Japan
[2] Hlth Sci Univ Hokkaido, Sch Dent, Dept Dent Mat Sci, Ishikari, Hokkaido 06102, Japan
[3] Hokkaido Univ, Grad Sch Dent Med, Div Pediat Dent, Sapporo, Hokkaido, Japan
[4] Hokkaido Univ, Grad Sch Dent Med, Div Cardiol & Endodontol, Sapporo, Hokkaido, Japan
[5] Univ Hong Kong, Fac Dent, Dept Conservat Dent, Hong Kong, Hong Kong, Peoples R China
关键词
fractography; micro-tensile bond test; hybrid layer; demineralized dentin;
D O I
10.1016/S0300-5712(02)00004-0
中图分类号
R78 [口腔科学];
学科分类号
1003 ;
摘要
Objectives. The purpose of this study was to determine (1) the weakest zone of resin-dentin bonds and (2) the relation between bond strength and failure mode to clarify the effect of demineralized dentin. Methods. Human premolars were sectioned to expose the dentin surfaces, and the dentin surfaces were conditioned with phosphoric acid for 15, 60, 120, or 180 s. Resin-dentin bonded specimens were produced using two adhesives: One-Step (Bisco) and OptiBond Solo (Kerr). Each sample was sectioned to produce a beam (adhesive area: 0.9 mm(2)). Microtensile bond tests were then conducted, and the mean bond strengths (n = 12 for each group) were statistically compared using two-way ANOVA and Duncan's multiple-range test (p < 0.05). The fractured surfaces of all specimens were examined using SEM, and the areas of failure were measured using an image analyzer. Results. For One-Step, the bond strength decreased with increase in acid-conditioning time (15 s: 50.7 +/- 9.7, 60 s: 40.8 +/- 11.0, 120 s: 23.6 +/- 4.9 and 180 s: 12.1 +/- 4.6 MPa) (p < 0.05). For OptiBond Solo, the bond strength in the case of 15 s acid-conditioning time (42.6 +/- 7.9 MPa) was significantly greater than that for the other times (60 s: 31.9 +/- 10.3, 120 s: 31.8 +/- 14.4 and 180 s: 31.8 +/- 7.4 MPa) (p < 0.05). Fractography showed that the area percentage of the hybrid layer increased with increase in etching time for both systems. Conclusions. The integrity of the hybrid layer, especially the top part, has an effect on bond strength. (C) 2002 Published by Elsevier Science Ltd.
引用
收藏
页码:99 / 105
页数:7
相关论文
共 22 条
[1]   Dentin bond durability after three years using a dentin bonding agent with and without priming [J].
Burrow, MF ;
Satoh, M ;
Tagami, J .
DENTAL MATERIALS, 1996, 12 (5-6) :302-307
[2]   Fractured surface characterization: wet versus dry bonding [J].
Hashimoto, M ;
Ohno, H ;
Kaga, M ;
Sano, H ;
Endo, K ;
Oguchi, H .
DENTAL MATERIALS, 2002, 18 (02) :95-102
[3]   The effect of hybrid layer thickness on bond strength: demineralized dentin zone of the hybrid layer [J].
Hashimoto, M ;
Ohno, H ;
Endo, K ;
Kaga, M ;
Sano, H ;
Oguchi, H .
DENTAL MATERIALS, 2000, 16 (06) :406-411
[4]   In vivo degradation of resin-dentin bonds in humans over 1 to 3 years [J].
Hashimoto, M ;
Ohno, H ;
Kaga, M ;
Endo, K ;
Sano, H ;
Oguchi, H .
JOURNAL OF DENTAL RESEARCH, 2000, 79 (06) :1385-1391
[5]   The influence of storage solution on dentin bond durability of resin cement [J].
Kitasako, Y ;
Burrow, MF ;
Nikaido, T ;
Tagami, J .
DENTAL MATERIALS, 2000, 16 (01) :1-6
[6]   EQUATORIAL DIFFRACTION SPACING AS A FUNCTION OF WATER-CONTENT IN FULLY MINERALIZED COW BONE DETERMINED BY NEUTRON-DIFFRACTION [J].
LEES, S ;
MOOK, HA .
CALCIFIED TISSUE INTERNATIONAL, 1986, 39 (04) :291-292
[7]   A tensile test to facilitate identification of defects in dentine bonded specimens [J].
Nakabayashi, N ;
Watanabe, A ;
Arao, T .
JOURNAL OF DENTISTRY, 1998, 26 (04) :379-385
[8]   EFFECT OF HEMA ON BONDING TO DENTIN [J].
NAKABAYASHI, N ;
TAKARADA, K .
DENTAL MATERIALS, 1992, 8 (02) :125-130
[9]  
NAKABAYASHI N, 1998, HYBRIDIZATION DENT H, P66
[10]  
Pashley D H, 1999, J Adhes Dent, V1, P299