An electrochemical impedance spectroscopy study of the corrosion behaviour of PVD coated steels in 0.5 N NaCl aqueous solution: Part II. EIS interpretation of corrosion behaviour

被引:589
作者
Liu, C [1 ]
Bi, Q
Leyland, A
Matthews, A
机构
[1] Loughborough Univ Technol, Wolfson Sch Mech & Mfg Engn, Loughborough LE11 3TU, Leics, England
[2] Univ Hull, Res Ctr Surface Engn, Kingston Upon Hull HU6 7RX, N Humberside, England
关键词
D O I
10.1016/S0010-938X(02)00214-7
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In Part I, of this work the equivalent circuits for electrochemical impedance spectroscopy (EIS) modelling of PVD coated steels in 0.5 NACl solution were established. In this paper, Part II, the EIS spectra of such coated systems are modelled using the equivalent circuits. The circuit parameters obtained are correlated with the dielectric characteristics, and microstructure of steels and PVD hard coatings. Coating porosity and localised corrosion with exposure time have also been determined using the corrosion potential difference (DeltaE(corr)) between mild steel and PVD coatings and polarisation resistance R-p, which was obtained through EIS modelling using equivalent circuits. In addition, diffusion rates of the reactants (e.g. oxygen) through 'permeable' defects (e.g. pores) are studied by introducing the diffusion impedances W and O in EIS modelling. It has been found that the usage of impedances W and O is closely related to the crystallite features of PVD coatings. Warburg impedance (W) is most suitable for columnar crystallites, while the co-tangent-hyperbolic diffusion impedance (O) is best for the equiaxed crystallite structure. Finally, visual inspection, SEM examination, and the scanning reference electrode technique were employed to observe the corrosion progress of PVD coated steels with immersion time, in order to validate the EIS interpretation. (C) 2002 Elsevier Science Ltd. All rights reserved.
引用
收藏
页码:1257 / 1273
页数:17
相关论文
共 30 条
[1]   EFFECT OF COMPOSITION AND THICKNESS ON CORROSION BEHAVIOR OF TIN AND ZRN THIN-FILMS [J].
BROWN, R ;
ALIAS, MN ;
FONTANA, R .
SURFACE & COATINGS TECHNOLOGY, 1993, 62 (1-3) :467-473
[2]   Corrosion of CrN and TiAlN coatings in chloride-containing atmospheres [J].
Cunha, L ;
Andritschky, M ;
Rebouta, L ;
Pischow, K .
SURFACE & COATINGS TECHNOLOGY, 1999, 116 :1152-1160
[3]   COMPARISON OF THE AC-IMPEDANCE OF CONDUCTING POLYMER-FILMS STUDIED AS ELECTRODE-SUPPORTED AND FREESTANDING MEMBRANES [J].
DESLOUIS, C ;
MUSIANI, MM ;
TRIBOLLET, B ;
VOROTYNTSEV, MA .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1995, 142 (06) :1902-1908
[4]  
Elsener B., 1989, MATER SCI FORUM, V44-45, P29, DOI [10.4028/www.scientific.net/MSF.44-45.29, DOI 10.4028/WWW.SCIENTIFIC.NET/MSF.44-45.29]
[5]   Corrosion and mechanical studies of chromium nitride films prepared by ion-beam-assisted deposition [J].
Engel, P ;
Schwarz, G ;
Wolf, GK .
SURFACE & COATINGS TECHNOLOGY, 1998, 98 (1-3) :1002-1007
[6]   Cementation as a method of observing defects in PVD coatings [J].
Ernst, P ;
Earnshaw, A ;
Wadsworth, IP ;
Marshall, GW .
CORROSION SCIENCE, 1997, 39 (07) :1329-1334
[7]  
FRANCESCHETTI DR, 1977, J ELECTROANAL CHEM, V82, P271, DOI 10.1016/0368-1874(77)80339-0
[8]   CEMS of nitride coatings in agressive environments [J].
Hanzel, D ;
Agudelo, AC ;
Gancedo, JR ;
Lakatos-Varsanyi, M ;
Marco, JF .
HYPERFINE INTERACTIONS, 1998, 111 (1-4) :93-100
[9]   Improvement of the corrosion resistance of PVD hard coating-substrate systems [J].
Jehn, HA .
SURFACE & COATINGS TECHNOLOGY, 2000, 125 (1-3) :212-217
[10]   Cyclic voltammetry measurements of different single-, bi- and multilayer TiN and single layer CrN coatings on low-carbon-steel substrates [J].
Lakatos-Varsanyi, M ;
Hanzel, D .
CORROSION SCIENCE, 1999, 41 (08) :1585-1598