Isotope dilution analysis for flow injection ICPMS determination of microgram per gram levels of boron in iron and steel after matrix removal

Isotope dilution analysis using now injection inductively coupled plasma mass spectrometry was applied to determine low boron contents in iron and steel samples, Sample dissolution was carried out in a microwave oven with an HC1, HNO3, and H2SO4 acid mixture and high-pressure digestion vessels, A solvent extraction procedure using acetylacetone-chloroform was applied for the separation of the iron matrix as the sulfate (pH = 1.4 +/- 0.1). Test solutions corresponding to 50 mg mL(-1) of sample, with the total boron content and iron contents below 1 mu g mL(-1), were obtained, Flow injection was used as a sampling system to minimize problems arising from the total salt concentration of the test solutions, This method made it possible to analyze boron in iron and steel at submicrogram per gram levels, The detection limit (3 sigma), in micrograms of boron per gram of sample, was 0.02, and the precision for concentrations above 10 times the detection limit was better than 1%, Accuracy was tested with eight standard reference materials with boron certified values in the 0.5-10 mu g g(-1) range.