A new observation on the phase transformation of TiO2 nanoparticles produced by a CVD method

被引：33

作者：

Kim, CS

Nakaso, K

Xia, B

Okuyama, K

Shimada, M

机构：

[1] Hiroshima Univ, Grad Sch Engn, Dept Chem Engn, Higashihiroshima 7398527, Japan

[2] Univ Minnesota, Dept Chem, Minneapolis, MN 55455 USA

来源：

AEROSOL SCIENCE AND TECHNOLOGY | 2005年 / 39卷 / 02期

基金：

日本学术振兴会;

关键词：

D O I：

10.1080/027868290906986

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

Titania (TiO2) nanoparticles with primary diameters of less than 30 nm were produced by the thermal decomposition of TTIP and by the oxidation of TiCl4 in a cylindrical furnace reactor at 1200degreesC. Particle size, crystalline phase, and phase transformation were investigated as a function of precursor concentration and total flow rate by TEM, a DMA/CNC system, XRD, and TG-DTA. The results show that both particle size and number concentration were increased with increasing precursor concentration, and that the primary size could be controlled by changing the operating conditions. An anatase-to-rutile phase transformation occurred at TTIP concentrations above 7.68 x 10(-6) mol/l and this was enhanced with increasing precursor concentration. It is noteworthy that the transformation is independent of grain size but appears to be related to the presence of carbon impurities in the nanoparticles.

引用

收藏

页码：104 / 112

页数：9

相关论文

共 17 条

[1] DOPANTS IN VAPOR-PHASE SYNTHESIS OF TITANIA POWDERS [J].

AKHTAR, MK ;

PRATSINIS, SE ;

MASTRANGELO, SVR .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1992, 75 (12) :3408-3416

[2] Aerosol synthesis of titania nanoparticles: Effect of flame orientation and configuration [J].

Arabi-Katbi, OI ;

Wegner, K ;

Pratsinis, SE .

ANNALES DE CHIMIE-SCIENCE DES MATERIAUX, 2002, 27 (06) :37-46

[3] Monitoring the flame synthesis of TiO2 particles by in-situ FTIR spectroscopy and thermophoretic sampling [J].

Arabi-Katbi, OI ;

Pratsinis, SE ;

Morrison, PW ;

Megaridis, CM .

COMBUSTION AND FLAME, 2001, 124 (04) :560-572

[4] Electrostatic precipitator for homogeneous deposition of ultrafine particles to create quantum-dot structures [J].

Deppert, Knut ;

Schmidt, Frank ;

Krinke, Thomas ;

Dixkens, Jörg ;

Fissan, Heinz .

Journal of Aerosol Science, 1996, 27 (SUPPL.1)

[5] Particle size effects on transformation kinetics and phase stability in nanocrystalline TiO2 [J].

Gribb, AA ;

Banfield, JF .

AMERICAN MINERALOGIST, 1997, 82 (7-8) :717-728

[6] Phase transformation of precipitated TiO2 nanoparticles [J].

Hu, Y ;

Tsai, HL ;

Huang, CL .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 344 (1-2) :209-214

[7] THE EFFECTS OF TEMPERATURE ON PARTICLE-SIZE IN THE GAS-PHASE PRODUCTION OF TIO2 [J].

JANG, HD ;

JEONG, J .

AEROSOL SCIENCE AND TECHNOLOGY, 1995, 23 (04) :553-560

[8] Direct measurement of nucleation and growth modes in titania nanoparticles generation by a CVD method [J].

Kim, CS ;

Okuyama, K ;

Nakaso, K ;

Shimada, M .

JOURNAL OF CHEMICAL ENGINEERING OF JAPAN, 2004, 37 (11) :1379-1389

[9] Effect of reaction temperature on CVD-made TiO2 primary particle diameter [J].

Nakaso, K ;

Okuyama, K ;

Shimada, M ;

Pratsinis, SE .

CHEMICAL ENGINEERING SCIENCE, 2003, 58 (15) :3327-3335

[10] Size distribution change of titania nano-particle agglomerates generated by gas phase reaction, agglomeration, and sintering [J].

Nakaso, K ;

Fujimoto, T ;

Seto, T ;

Shimada, M ;

Okuyama, K ;

Lunden, MM .

AEROSOL SCIENCE AND TECHNOLOGY, 2001, 35 (05) :929-947