Infrared and electrical properties of amorphous sputtered (LaxAl1-x)2O3 films

被引：38
作者：
Devine, RAB
机构：
[1] USAF, Res Lab, Space Vehicles Directorate, Kirtland AFB, NM 87117 USA
[2] Univ New Mexico, Ctr High Technol Mat, Albuquerque, NM 87106 USA
来源：
JOURNAL OF APPLIED PHYSICS | 2003年 / 93卷 / 12期
关键词：
D O I：
10.1063/1.1576299
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
Amorphous (LaxAl1-x)(2)O-3 (0.61less than or equal toxless than or equal to0.73) films have been deposited by sputtering in a partially reactive atmosphere. The average dielectric constant of the as-deposited films was 13.4 and 12.5 following annealing at 700 degreesC for 60 min in N-2; both values were much lower than the single crystal values similar to24 and 28 for LaAlO3 and La2O3, respectively. Leakage current densities were similar to10(-8) A cm(-2) for an applied field of 1 MV cm(-1) for film thicknesses similar to75 nm. Fourier transform infrared spectroscopy reveals transverse optic mode peaks at 723 and 400 cm(-1) and corresponding longitudinal optic modes at 821 and 509 cm(-1). The density of the amorphous phase is estimated to be similar to0.9 times the crystalline density. (C) 2003 American Institute of Physics.
引用
收藏
页码：9938 / 9942
页数：5
相关论文
共 18 条
[1]   Comparative study of optical phonons in the rhombohedrally distorted perovskites LaAlO3 and LaMnO3 [J].
Abrashev, MV ;
Litvinchuk, AP ;
Iliev, MN ;
Meng, RL ;
Popov, VN ;
Ivanov, VG ;
Chakalov, RA ;
Thomsen, C .
PHYSICAL REVIEW B, 1999, 59 (06) :4146-4153
[2]  
BARKER AS, 1966, PHYS REV, V136, pA1290
[3]   INFRARED ABSORPTION AT LONGITUDINAL OPTIC FREQUENCY IN CUBIC CRYSTAL FILMS [J].
BERREMAN, DW .
PHYSICAL REVIEW, 1963, 130 (06) :2193-&
[4]  
BUNGET I, 1984, PHYSICS SOLID DIELEC, pCH6
[5]   Theoretical structure determination of γ-Al2O3 -: art. no. 012101 [J].
Gutiérrez, G ;
Taga, A ;
Johansson, B .
PHYSICAL REVIEW B, 2002, 65 (01) :1-4
[6]   A nuclear magnetic resonance study of amorphous and crystalline lanthanum-aluminates [J].
Iuga, D ;
Simon, S ;
de Boer, E ;
Kentgens, APM .
JOURNAL OF PHYSICAL CHEMISTRY B, 1999, 103 (36) :7591-7598
[7]   Dielectric functions and optical bandgaps of high-K dielectrics for metal-oxide-semiconductor field-effect transistors by far ultraviolet spectroscopic ellipsometry [J].
Lim, SG ;
Kriventsov, S ;
Jackson, TN ;
Haeni, JH ;
Schlom, DG ;
Balbashov, AM ;
Uecker, R ;
Reiche, P ;
Freeouf, JL ;
Lucovsky, G .
JOURNAL OF APPLIED PHYSICS, 2002, 91 (07) :4500-4505
[8]   Refractive index and optical dispersion of rare earth oxides using a small-prism technique [J].
Medenbach, O ;
Dettmar, D ;
Shannon, RD ;
Fischer, RX ;
Yen, WM .
JOURNAL OF OPTICS A-PURE AND APPLIED OPTICS, 2001, 3 (03) :174-177
[9]   Interfacial reactions between thin rare-earth-metal oxide films and Si substrates [J].
Ono, H ;
Katsumata, T .
APPLIED PHYSICS LETTERS, 2001, 78 (13) :1832-1834
[10]   Electrical properties of LaAlO3/Si and Sr0.8Bi2.2Ta2O9/LaAlO3/Si structures [J].
Park, BE ;
Ishiwara, H .
APPLIED PHYSICS LETTERS, 2001, 79 (06) :806-808
12