Hydrotalcite conversion coating on Mg alloy and its corrosion resistance

被引：109

作者：

Wang, Jun ^{[1
,2
]}

Li, Dandan ^{[1
]}

Yu, Xiang

Jing, Xiaoyan ^{[1
]}

Zhang, Milin ^{[1
]}

Jiang, Zhaohua ^{[2
]}

机构：

[1] Harbin Engn Univ, Coll Mat Sci & Chem Engn, Harbin 150001, Peoples R China

[2] Harbin Inst Technol, Coll Chem Engn, Harbin 150001, Peoples R China

来源：

JOURNAL OF ALLOYS AND COMPOUNDS | 2010年 / 494卷 / 1-2期

关键词：

Mg-Al LDH film; Conversion coating; Mg alloy; Corrosion resistance; NI-P; MAGNESIUM ALLOY; THIN-FILMS; BEHAVIOR; SURFACE; AZ91; PRECIPITATION; DEPOSITION; MECHANISM; ALUMINUM;

D O I：

10.1016/j.jallcom.2010.01.007

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

A magnesium-aluminum layered double hydroxide (Mg-Al LDH) film was fabricated on a Mg alloy substrate by a hydrothermal crystallization method, based on an interface reaction between hydrotalcite slurry and Mg alloy. Magnesium-aluminum layered double hydroxide with carbonate intercalation was obtained by synthesis involving separate nucleation and aging steps, where the Mg-Al LDH film was formed in the aging process. The LDH film was uniform and compact. The film was characterized by XRD, SEM, EDS techniques to study the structure, phase purity and morphology, respectively. Polarization measurements and electrochemical impedance spectroscopy (EIS) showed that the LDH film could effectively protect Mg alloy from corrosion. The cross cutting showed that the adhesion between the film and the substrate was very strong which enhances its potential for practical application. (C) 2010 Elsevier B.V. All rights reserved.

引用

页码：271 / 274

页数：4

共 35 条

[1] Corrosion protection of AZ91 magnesium alloy by anodizing in niobium and zirconium-containing electrolytes [J].

Ardelean, H. ;

Frateur, I. ;

Zanna, S. ;

Atrens, A. ;

Marcus, P. .

CORROSION SCIENCE, 2009, 51 (12) :3030-3038

[2] Anodization of Mg-alloy AZ91 in NaOH solutions [J].

Barbosa, D. Peixoto ;

Knornschild, G. .

SURFACE & COATINGS TECHNOLOGY, 2009, 203 (12) :1629-1636

[3] The relation between severe plastic deformation microstructure and corrosion behavior of AZ31 magnesium alloy [J].

Ben Hamu, G. ;

Eliezer, D. ;

Wagner, L. .

JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 468 (1-2) :222-229

[4] EIS studies of coated metals in accelerated exposure [J].

Bierwagen, G ;

Tallman, D ;

Li, JP ;

He, LY ;

Jeffcoate, C .

PROGRESS IN ORGANIC COATINGS, 2003, 46 (02) :148-157

[5] Active metal-based corrosion protective coating systems for aircraft requiring no-chromate pretreatment [J].

Bierwagen, Gordon ;

Brown, Roger ;

Battocchi, Dante ;

Hayes, Scott .

PROGRESS IN ORGANIC COATINGS, 2010, 67 (02) :195-208

[6] Corrosion resistance of thermally sprayed Al and Al/SiC coatings on Mg [J].

Campo, M. ;

Carboneras, M. ;

Lopez, M. D. ;

Torres, B. ;

Rodrigo, P. ;

Otero, E. ;

Rams, J. .

SURFACE & COATINGS TECHNOLOGY, 2009, 203 (20-21) :3224-3230

[7] Protective coating on Mg AZ91D alloy - The effect of electroless nickel (EN) bath stabilizers on corrosion behaviour of Ni-P deposit [J].

Cheong, Woo-Jae ;

Luan, Ben L. ;

Shoesmith, David W. .

CORROSION SCIENCE, 2007, 49 (04) :1777-1798

[8] Effects of pH and temperature on the deposition properties of stannate chemical conversion coatings formed by the potentiostatic technique on AZ91 D magnesium alloy [J].

Elsentriecy, Hassan H. ;

Azumi, Kazuhisa ;

Konno, Hidetaka .

ELECTROCHIMICA ACTA, 2008, 53 (12) :4267-4275

[9] A guide to polarisation curve interpretation:: deconstruction of experimental curves typical of the Fe/H2O/H+/O2 corrosion system [J].

Flitt, HJ ;

Schweinsberg, DP .

CORROSION SCIENCE, 2005, 47 (09) :2125-2156

[10] The corrosion of a novel Mg-11Li-3Al-0.5RE alloy in alkaline NaCl solution [J].

Gao, Lili ;

Zhang, Chunhong ;

Zhang, Milin ;

Huang, Xiaomei ;

Sheng, Nan .

JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 468 (1-2) :285-289

← 1 2 3 4 →