Sputter deposition of bcc tantalum films with TaN underlayers for protection of steel

被引:66
作者
Gladczuk, L
Patel, A
Demaree, JD
Sosnowski, M [1 ]
机构
[1] New Jersey Inst Technol, Dept Elect & Comp Engn, Newark, NJ 07102 USA
[2] USA, Res Lab, Aberdeen Proving Ground, MD 21005 USA
关键词
physical vapor deposition; tantalum; tantalum nitride; magnetron sputtering;
D O I
10.1016/j.tsf.2004.10.020
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Deposition of tantalum films for protective coatings on steel has been investigated. The desired tough and ductile bcc phase of tantalum, rather than the normally deposited hard and brittle tetragonal phase, has been grown by DC magnetron sputtering on unheated substrates first covered with thin layers of tantalum nitride. The nitride was formed by reactive sputtering with nitrogen gas, with the same DC magnetron source and target as used for deposition of tantalum. The crystal structure and composition of the nitride promoting the growth of bcc Ta, previously undefined, has been identified as the metastable fcc (NaCl like) TaN. Alignment of the (111) crystallographic planes of fec TAN with (110) planes of bcc Ta is discussed as a possible mechanism for this effect. The minimum thickness of TaN underlayer on steel, required to promote the growth of bcc Ta, has been established and found to be dependent on the substrate surface preparation. Scratch tests with a diamond tip showed that the nitride underlayer does not compromise the film adhesion. Stable and well-adhering coatings of bcc Ta with thickness ranging from tens of nanometers to tens of micrometers on steel with a thin TaN underlayer were obtained. The process of deposition of bcc Ta films, including the formation of TAN underlayers is described in detail. (c) 2004 Elsevier B.V. All rights reserved.
引用
收藏
页码:295 / 302
页数:8
相关论文
共 26 条
[1]  
BROSSA F, 1982, J NUCL MATER, V103, P261
[2]   LOW RESISTIVITY BODY-CENTERED CUBIC TANTALUM THIN-FILMS AS DIFFUSION-BARRIERS BETWEEN COPPER AND SILICON [J].
CATANIA, P ;
DOYLE, JP ;
CUOMO, JJ .
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1992, 10 (05) :3318-3321
[3]   Growth mechanism of sputter deposited Ta and Ta-N thin films induced by an underlying titanium layer and varying nitrogen flow rates [J].
Chen, GS ;
Chen, ST ;
Huang, SC ;
Lee, HY .
APPLIED SURFACE SCIENCE, 2001, 169 :353-357
[4]   THE RELATIONSHIP BETWEEN DEPOSITION CONDITIONS, THE BETA TO ALPHA PHASE-TRANSFORMATION, AND STRESS-RELAXATION IN TANTALUM THIN-FILMS [J].
CLEVENGER, LA ;
MUTSCHELLER, A ;
HARPER, JME ;
CABRAL, C ;
BARMAK, K .
JOURNAL OF APPLIED PHYSICS, 1992, 72 (10) :4918-4924
[5]  
COLGAN EG, 1993, Patent No. 5221449
[6]  
EDELSTEIN D, 1997, J ELECT DEV M, P773
[7]   LOW-TEMPERATURE FORMATION OF METASTABLE CUBIC TANTALUM NITRIDE BY METAL CONDENSATION UNDER ION IRRADIATION [J].
ENSINGER, W ;
KIUCHI, M ;
SATOU, M .
JOURNAL OF APPLIED PHYSICS, 1995, 77 (12) :6630-6635
[8]   NUCLEATION OF BODY-CENTERED-CUBIC TANTALUM FILMS WITH A THIN NIOBIUM UNDERLAYER [J].
FACE, DW ;
PROBER, DE .
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1987, 5 (06) :3408-3411
[9]   The proliferation and phenotypic expression of human osteoblasts on tantalum metal [J].
Findlay, DM ;
Welldon, K ;
Atkins, GJ ;
Howie, DW ;
Zannettino, ACW ;
Bobyn, D .
BIOMATERIALS, 2004, 25 (12) :2215-2227
[10]   Tantalum films for protective coatings of steel [J].
Gladczuk, L ;
Patel, A ;
Paur, CS ;
Sosnowski, M .
THIN SOLID FILMS, 2004, 467 (1-2) :150-157