A note on fracture criteria for interface fracture

被引：69

作者：

Banks-Sills, L ^{[1
]}

Ashkenazi, D ^{[1
]}

机构：

[1] Tel Aviv Univ, Fleischman Fac Engn, Dept Solid Mech Mat & Struct, Dreszer Fracture Mech Lab, IL-69978 Tel Aviv, Israel

来源：

INTERNATIONAL JOURNAL OF FRACTURE | 2000年 / 103卷 / 02期

关键词：

fracture criteria; interface fracture mechanics; interface fracture toughness;

D O I：

10.1023/A:1007612613338

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Several criteria for interface fracture are examined and compared to test results obtained from glass/epoxy specimens. These include two energy release rate criteria, a critical hoop stress criterion and a critical shear stress criterion. In addition, approximate plastic zone size and shape within the epoxy are determined for these tests.

引用

收藏

页码：177 / 188

页数：12

相关论文

共 10 条

[1] A methodology for measuring interface fracture properties of composite materials [J].

Leslie Bank-Sills ;

Nahum Travitzky ;

Dana Ashkenazi ;

Rami Eliasi .

International Journal of Fracture, 1999, 99 (3) :143-161

[2]

CHARALAMBIDES M, 1992, INT J FRACTURE, V54, P269

[3] GENERAL CRACK-TIP FIELDS FOR STATIONARY AND STEADILY GROWING INTERFACE CRACKS IN ANISOTROPIC BIMATERIALS [J].

DENG, X .

JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME, 1993, 60 (01) :183-189

[4] CRACK-PROPAGATION AT AND NEAR BIMATERIAL INTERFACES - LINEAR-ANALYSIS [J].

GEUBELLE, PH ;

KNAUSS, WG .

JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME, 1994, 61 (03) :560-566

[5] MIXED-MODE CRACKING IN LAYERED MATERIALS [J].

HUTCHINSON, JW ;

SUO, Z .

ADVANCES IN APPLIED MECHANICS, VOL 29, 1992, 29 :63-191

[6] ASYMMETRIC SHIELDING IN INTERFACIAL FRACTURE UNDER INPLANE SHEAR [J].

LIECHTI, KM ;

CHAI, YS .

JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME, 1992, 59 (02) :295-304

[7]

Rice J.R., 1990, Acta-Scr. Metall. Proc. Ser., V4, P269, DOI DOI 10.1016/B978-0-08-040505-6.50036-2

[8] Asymmetric shielding mechanisms in the mixed-mode fracture of a glass/epoxy interface [J].

Swadener, JG ;

Liechti, KM .

JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME, 1998, 65 (01) :25-29

[9] Nickel-alumina interfacial fracture toughness: Experiments and analysis of residual stress effects [J].

Thurston, ME ;

Zehnder, AT .

INTERNATIONAL JOURNAL OF FRACTURE, 1996, 76 (03) :221-241

[10] Fracture of interface cracks under combined loading [J].

Wang, CH .

ENGINEERING FRACTURE MECHANICS, 1997, 56 (01) :77-86