Development and thermal fatigue testing of ceramic thermal barrier coatings

被引:48
作者
Zhu, DM [1 ]
Choi, SR [1 ]
Miller, RA [1 ]
机构
[1] NASA, Johns H Gleen Res Ctr, Surface & Protect Coatings Branch, Cleveland, OH 44135 USA
基金
美国国家航空航天局;
关键词
thermal barrier coatings; thermal conductivity; thermal fatigue; high power laser; crack propagation; coating spallation; life prediction;
D O I
10.1016/j.surfcoat.2004.08.017
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Ceramic thermal barrier coatings (TBCs) will play an increasingly important role in future gas turbine engines because of their ability to effectively protect the engine components and further raise engine temperatures. Durability of the coating systems remains a critical issue with the ever-increasing temperature requirements. Thermal conductivity increase and coating degradation due to sintering and phase changes are known to be detrimental to coating performance. There is a need to characterize the coating thermal fatigue behavior and temperature limit, in order to potentially take full advantage of the current coating capability. In this study, a laser thermal fatigue test technique has been used to study the delamination crack propagation of thermal barrier coatings under simulated engine heat flux heating and thermal cyclic loading. Thermal conductivity and cyclic fatigue behaviors of plasma-sprayed ZrO2-8 wt-% Y2O3 thermal barrier coatings were evaluated under high temperature, large thermal gradient and thermal cycling conditions. The coating degradation and failure processes were assessed by real-time monitoring of the coating thermal conductivity during the testing. The test results showed that the initial average crack propagation rates of ZrO2-8 Wt-% Y2O3 coatings were in the range of 3-8 mum/cycle. The crack propagation rates increased to 30-40 mum/cycle at later stages of testing, and the critical spalling crack size ranged from 3 to 5 mm for the coatings. The accelerated crack growth is attributed to the increased driving force for crack propagation under the laser heat flux cyclic test conditions. (C) 2004 Elsevier B.V. All rights reserved.
引用
收藏
页码:146 / 152
页数:7
相关论文
共 17 条
[1]  
Choi S. R., 1999, Ceramic Engineering and Science Proceedings, V20, P365
[2]  
Choi SR, 1998, CERAM ENG SCI PROC, V19, P293
[3]   Mechanical properties testing and results for thermal barrier coatings [J].
Cruse, TA ;
Johnsen, BP ;
Nagy, A .
JOURNAL OF THERMAL SPRAY TECHNOLOGY, 1997, 6 (01) :57-66
[4]   ON THE MECHANICS OF DELAMINATION AND SPALLING IN COMPRESSED FILMS [J].
EVANS, AG ;
HUTCHINSON, JW .
INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 1984, 20 (05) :455-466
[5]   Relationships between residual stress, microstructure and mechanical properties of electron beam physical vapor deposition thermal barrier coatings [J].
Johnson, CA ;
Ruud, JA ;
Bruce, R ;
Wortman, D .
SURFACE & COATINGS TECHNOLOGY, 1998, 108 (1-3) :80-85
[6]   Deformation behavior of plasma-sprayed thick thermal barrier coatings [J].
Rejda, EF ;
Socie, DF ;
Itoh, T .
SURFACE & COATINGS TECHNOLOGY, 1999, 113 (03) :218-226
[7]   Fatigue behavior of a plasma-sprayed 8%Y2O3-ZrO2 thermal barrier coating [J].
Rejda, EF ;
Socie, DF ;
Beardsley, B .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1997, 20 (07) :1043-1050
[8]   High-temperature deformation of plasma-sprayed ZrO2 thermal barrier coatings [J].
Thurn, G ;
Schneider, GA ;
Aldinger, F .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 233 (1-2) :176-182
[9]  
Timoshenko S.P., 1970, THEORY ELASTIC STABI, V3rd
[10]  
ZHU D, 2001, INT C MET COAT THIN