Humidity sensing properties of BaTiO3 nanofiber prepared via electrospinning

被引：175

作者：

He, Yuan ^{[1
]}

Zhang, Tong ^{[1
]}

Zheng, Wei ^{[1
]}

Wang, Rui ^{[1
]}

Liu, Xiangwei ^{[1
]}

Xia, Yan ^{[1
]}

Zhao, Jinwei ^{[1
]}

机构：

[1] Jilin Univ, Coll Elect Sci & Engn, State Key Lab Integrated Optoelect, Changchun 130012, Peoples R China

来源：

SENSORS AND ACTUATORS B-CHEMICAL | 2010年 / 146卷 / 01期

基金：

中国国家自然科学基金;

关键词：

Electrospinning; BaTiO3; Nanofiber; Humidity sensing; Sensor; BOMBYX-MORI SILK; BARIUM-TITANATE; ELECTRICAL-PROPERTIES; POLYMER QAR; FIBERS; SENSOR; GEL; NANOWIRES; COMPOSITE; FABRICATION;

D O I：

10.1016/j.snb.2010.02.030

中图分类号：

O65 [分析化学];

学科分类号：

070302 [分析化学];

摘要：

Barium titanate (BaTiO3) nanofiber was synthesized by electrospinning and by using the calcinations technique. Its morphologies were characterized by scanning electron microscopy, which showed that its average diameter was 80-200 nm, and its length was over 0.1 mm. An impedance-type humidity sensor was then fabricated based on this BaTiO3 nanofiber. It was unexpected to find that such sensor exhibited fast response and recovery, which were 5 and 4s between 11% and 95% relative humidity, respectively. The long stability and humidity hysteresis properties of this sensor were also tested, and they were found to be optimum. These excellent sensing characteristics prove that BaTiO3 nanofiber is applicable for high-performance humidity sensors. (C) 2010 Elsevier B.V. All rights reserved.

引用

页码：98 / 102

页数：5