The strength and toughness of cement reinforced with bone-shaped steel wires

被引：31

作者：

Jiang, HG ^{[1
]}

Valdez, JA ^{[1
]}

Zhu, YT ^{[1
]}

Beyerlein, IJ ^{[1
]}

Lowe, TC ^{[1
]}

机构：

[1] Univ Calif Los Alamos Natl Lab, Div Mat Sci & Technol, Los Alamos, NM 87545 USA

来源：

COMPOSITES SCIENCE AND TECHNOLOGY | 2000年 / 60卷 / 09期

关键词：

short-fiber composites; strength; toughness; fiber bridging; BSS wires;

D O I：

10.1016/S0266-3538(00)00055-5

中图分类号：

TB33 [复合材料];

学科分类号：

摘要：

In this study, we have experimentally evaluated the effectiveness of bone-shaped short (BSS) steel wire reinforcement in improving the mechanical properties of cement. Results from four-point bending tests revealed that BSS-steel-wire-reinforced cement is substantially stronger, tougher, and more crack resistant than conventional straight short (CSS) steel-wire-reinforced cement and unreinforced cement. The BSS steel wires provided effective crack bridging by a combination of their ductility and the mechanical interlocking between their enlarged spherical ends and the cement matrix. In the BSS-wire-reinforced cement specimens, multiple cracks formed along the length of the specimen before final failure, whereas in the CSS-wire-reinforced cement and unreinforced cement specimens, a single central crack initiated and propagated across the specimen. Some BSS wires bridged the main crack and were eventually plastically deformed to failure. Secondary matrix cracks also radiated away from the main fracture surfaces, providing significant contributions to the toughness of the composites. In contrast, the bridging CSS wires were easily pulled out of the matrix without much deformation in the wire itself and surrounding cement. Therefore, they were not nearly as effective in bridging cracks and improving toughness as the BSS wires. (C) 2000 Elsevier Science Ltd. AU rights reserved.

引用

页码：1753 / 1761

页数：9

共 31 条

[1]

*ACI COMM 544, 1997, FIB REINF CONCR

[2]

*ACI COMM 544, 5441 ACI COMM 544

[3] FIBER TOUGHENING OF MDF CEMENT [J].

ALFORD, NM ;

BIRCHALL, JD .

JOURNAL OF MATERIALS SCIENCE, 1985, 20 (01) :37-45

[4]

[Anonymous], FRACTURE SIZE EFFECT

[5]

*ASTM, 134197 ASTM C

[6]

AVERY C, 1975, CONCRETE CONSTR, P355

[7]

Aveston J., 1971, IPC Science and Technology Press, P15

[8] MULTIPLE CRACKING IN ALIGNED POLYPROPYLENE FIBER REINFORCED CEMENT COMPOSITES [J].

BAGGOTT, R ;

GANDHI, D .

JOURNAL OF MATERIALS SCIENCE, 1981, 16 (01) :65-74

[9]

BALAGURU PN, 1992, FIBER REINFORCED CEM, P530

[10] PROPAGATION OF CRACKS IN COMPOSITES CONSISTING OF DUCTILE WIRES IN A BRITTLE MATRIX [J].

BOWLING, J ;

GROVES, GW .

JOURNAL OF MATERIALS SCIENCE, 1979, 14 (02) :443-449

← 1 2 3 4 →