Fluorination of carbon nanotubes

被引：12

作者：

Hamwi, A ^{[1
]}

Alvergnat, H ^{[1
]}

Bonnamy, S ^{[1
]}

Beguin, F ^{[1
]}

机构：

[1] UNIV ORLEANS,CTR RECH MAT DIVISEE,CNRS,F-45071 ORLEANS 2,FRANCE

来源：

CARBON | 1997年 / 35卷 / 06期

关键词：

nanotubes; fluorination; electron microscopy; X-ray diffraction;

D O I：

暂无

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

Carbon nanotubes were prepared by thermal decomposition of acetylene over silica-supported cobalt catalysts. Subsequent chemical treatments with concentrated hydrofluoric acid and dilute nitric acid, respectively, eliminated the silica substrate and the remaining catalyst. The complete removal of cobalt was very difficult due to encapsulation of part of it in the shells, but a graphitization at 2800 degrees C eliminated the rest of cobalt and the structural defects. The reactivity of carbon nanotubes with fluorine was studied and compared to that of graphite. Important modification of the nanotubes structure was observed after reaction at high temperature as against the behaviour observed during reaction at room temperature. Compounds were analysed by means of transmission electron microscopy, X-ray diffraction and Fourier transform infrared spectroscopy. (C) 1997 Elsevier Science Ltd.

引用

页码：723 / 728

页数：6

共 13 条

[1]

ALVERGNAT H, 1996, P CARB 96, V2, P715

[2]

Baker R.T.K., 1978, CHEM PHYS CARBON, V14, P83

[3] PYROLYTIC CARBON NANOTUBES FROM VAPOR-GROWN CARBON-FIBERS [J].

ENDO, M ;

TAKEUCHI, K ;

KOBORI, K ;

TAKAHASHI, K ;

KROTO, HW ;

SARKAR, A .

CARBON, 1995, 33 (07) :873-881

[4] Fluorine reactivity with graphite and fullerenes. Fluoride derivatives and some practical electrochemical applications [J].

Hamwi, A .

JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 1996, 57 (6-8) :677-688

[5] GRAPHITE FLUORIDES PREPARED AT ROOM-TEMPERATURE .1. SYNTHESIS AND CHARACTERIZATION [J].

HAMWI, A ;

DAOUD, M ;

COUSSEINS, JC .

SYNTHETIC METALS, 1988, 26 (01) :89-98

[6] F-19 NMR-STUDY OF GRAPHITE FLUORIDES PREPARED AT ROOM-TEMPERATURE [J].

HAMWI, A ;

DAOUD, M ;

DJURADO, D ;

COUSSEINS, JC ;

FAWAL, Z ;

DUPUIS, J .

SYNTHETIC METALS, 1991, 44 (01) :75-83

[7] HELICAL MICROTUBULES OF GRAPHITIC CARBON [J].

IIJIMA, S .

NATURE, 1991, 354 (6348) :56-58

[8] THE STUDY OF CARBON NANOTUBULES PRODUCED BY CATALYTIC METHOD [J].

IVANOV, V ;

NAGY, JB ;

LAMBIN, P ;

LUCAS, A ;

ZHANG, XB ;

ZHANG, XF ;

BERNAERTS, D ;

VANTENDELOO, G ;

AMELINCKX, S ;

VANLANDUYT, J .

CHEMICAL PHYSICS LETTERS, 1994, 223 (04) :329-335

[9] CATALYTIC GROWTH OF CARBON MICROTUBULES WITH FULLERENE STRUCTURE [J].

JOSEYACAMAN, M ;

MIKIYOSHIDA, M ;

RENDON, L ;

SANTIESTEBAN, JG .

APPLIED PHYSICS LETTERS, 1993, 62 (02) :202-204

[10] CHEMICAL COMPOSITION AND CRYSTAL-STRUCTURE OF GRAPHITE FLUORIDE [J].

KITA, Y ;

WATANABE, N ;

FUJII, Y .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1979, 101 (14) :3832-3841

← 1 2 →