Synthesis and characterization of Cu-Co-Fe hydrotalcites and their calcined products

被引：25

作者：

Carpentier, J. ^{[1
]}

Siffert, S. ^{[1
]}

Lamonier, J. F. ^{[1
]}

Laversin, H. ^{[1
]}

Aboukais, A. ^{[1
]}

机构：

[1] Univ Littoral Cote dOpale, Lab Catalyse & Environm, MREI, EA 2598, F-59140 Dunkerque, France

来源：

JOURNAL OF POROUS MATERIALS | 2007年 / 14卷 / 01期

关键词：

Cu-Co-Fe hydrotalcite; spinel; XRD; XPS; TG-DTA;

D O I：

10.1007/s10934-006-9014-1

中图分类号：

O69 [应用化学];

学科分类号：

081704 ;

摘要：

A series of new Cu-Co-Fe compounds with the general formula Cu Co-x(2-x) Fe1HT (x = 0, 0.5, 1, 1.5 and 2) has been prepared by hydrotalcite coprecipitation method. The presence of hydrotalcite phase is revealed by XRD analysis for x values of 0, 0.5 and 1. When the copper quantity is higher than 1, the malachite phase is preferentially formed. These results are confirmed by TG-DTA, FT-IR and XPS analysis. After calcination at 500 degrees C in air of all samples, XRD analysis reveals the presence of spinel phases such as Co3O4, CoFe2O4, CuFe2O4, Cu xCoyO4 in the solids, monoclinic CuO phase when the copper content is greater or equal to 1 and haematite phase for the sample where x is equal to 2. The presence of these phases is also confirmed by XPS results. For comparison, a Co2Fe1OH sample has been synthesized by classical coprecipitation method and although Co2Fe1HT sample and Co2Fe1OH form a similar phase after calcination at 500 degrees C, Co(2)Fe(1)HT500 presents a higher BET value than Co(2)Fe(1)OH500 sample.

引用

页码：103 / 110

页数：8

共 36 条

[1] Preparation and activity of Cu-Al mixed oxides via hydrotalcite-like precursors for the oxidation of phenol aqueous solutions [J].

Alejandre, A ;

Medina, F ;

Rodriguez, X ;

Salagre, P ;

Sueiras, JE .

JOURNAL OF CATALYSIS, 1999, 188 (02) :311-324

[2] Magnesium salts and oxide: an XPS overview [J].

Ardizzone, S ;

Bianchi, CL ;

Fadoni, M ;

Vercelli, B .

APPLIED SURFACE SCIENCE, 1997, 119 (3-4) :253-259

[3] Heterogeneous coupling of phenylethyne over Cu-Mg-Al mixed oxides - Influence of catalyst composition and calcination temperature on structural and catalytic properties [J].

Auer, SM ;

Wandeler, R ;

Gobel, U ;

Baiker, A .

JOURNAL OF CATALYSIS, 1997, 169 (01) :1-12

[4] LDH-derived catalysts for complete oxidation of volatile organic compounds [J].

Bahranowski, K ;

Bielanska, E ;

Janik, R ;

Machej, T ;

Serwicka, EM .

CLAY MINERALS, 1999, 34 (01) :67-77

[5] Oxidation of aromatic hydrocarbons with hydrogen peroxide over Zn,Cu,Al-layered double hydroxides [J].

Bahranowski, K ;

Dula, R ;

Gasior, M ;

Labanowska, M ;

Michalik, A ;

Vartikian, LA ;

Serwicka, EM .

APPLIED CLAY SCIENCE, 2001, 18 (1-2) :93-101

[6] XPS and TPR examinations of γ-alumina-supported Pd-Cu catalysts [J].

Batista, J ;

Pintar, A ;

Mandrino, D ;

Jenko, M ;

Martin, V .

APPLIED CATALYSIS A-GENERAL, 2001, 206 (01) :113-124

[7] Copper and iron substituted hydrotalcites: properties and catalyst precursors for methylamines synthesis [J].

Carja, G ;

Nakamura, R ;

Niiyama, H .

APPLIED CATALYSIS A-GENERAL, 2002, 236 (1-2) :91-102

[8] Textural properties of layered double hydroxides: effect of magnesium substitution by copper or iron [J].

Carja, G ;

Nakamura, R ;

Aida, T ;

Niiyama, H .

MICROPOROUS AND MESOPOROUS MATERIALS, 2001, 47 (2-3) :275-284

[9] Characterisation of Mg/Al hydrotalcite with interlayer palladium complex for catalytic oxidation of toluene [J].

Carpentier, J ;

Lemonier, JF ;

Siffert, S ;

Zhilinskaya, EA ;

Aboukaïis, A .

APPLIED CATALYSIS A-GENERAL, 2002, 234 (1-2) :91-101

[10] HYDROTALCITE-TYPE ANIONIC CLAYS: PREPARATION, PROPERTIES AND APPLICATIONS [J].

Cavani, F. ;

Trifiro, F. ;

Vaccari, A. .

CATALYSIS TODAY, 1991, 11 (02) :173-301

← 1 2 3 4 →