Analyses of capacity loss and improvement of cycle performance for a high-voltage hybrid electrochemical capacitor

被引:70
作者
Aida, Taira
Murayama, Ichiro
Yamada, Koji
Morita, Masayuki
机构
[1] Maihatsu Motor Co Ltd, Adv Tech Dev Div, Shiga 5202593, Japan
[2] Yamaguchi Univ, Grad Sch Sci & Engn, Dept Appl Chem, Ube, Yamaguchi 7558611, Japan
关键词
D O I
10.1149/1.2746562
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
A high-voltage hybrid electrochemical capacitor (HEC) which uses nongraphitizable carbon for a negative electrode and activated carbon for a positive electrode has been constructed with lithium salt for the electrolyte. Under high-voltage conditions, large capacity loss during charge-discharge cycling was observed when the positive electrode was highly polarized at a potential over 4 V vs Li/Li+. This capacity loss was induced by the increase of the interfacial resistance at the negative electrode. A large amount of lithium fluoride (LiF) was observed on the surface of the negative electrode after charge-discharge cycling. It is considered that the LiF was generated by a reaction of hydrofluoric acid (HF), generated by the decomposition of hexafluorophosphate anion (PF6-), with lithium alkyl carbonate (semicarbonate, ROCOOLi) or lithium carbonate (Li2CO3) on the surface of the negative electrode. The generation of LiF and the capacity loss were suppressed by providing lithium metal between the positive electrode and the negative electrode. It was thus confirmed that the suppression of LiF generation, caused by high polarization of activated carbon positive electrode, can realize a high-voltage HEC with good cycleability. (c) 2007 The Electrochemical Society.
引用
收藏
页码:A798 / A804
页数:7
相关论文
共 31 条
  • [1] Improvement in cycle performance of a high-voltage hybrid electrochemical capacitor
    Aida, Taira
    Murayama, Ichiro
    Yamada, Koji
    Morita, Masayuki
    [J]. ELECTROCHEMICAL AND SOLID STATE LETTERS, 2007, 10 (04) : A93 - A96
  • [2] An advanced hybrid electrochemical capacitor that uses a wide potential range at the positive electrode
    Aida, Taira
    Yamada, Koji
    Morita, Masayuki
    [J]. ELECTROCHEMICAL AND SOLID STATE LETTERS, 2006, 9 (12) : A534 - A536
  • [3] An asymmetric hybrid nonaqueous energy storage cell
    Amatucci, GG
    Badway, F
    Du Pasquier, A
    Zheng, T
    [J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2001, 148 (08) : A930 - A939
  • [4] Chemical composition and morphology of the elevated temperature SEI on graphite
    Andersson, AM
    Edström, K
    [J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2001, 148 (10) : A1100 - A1109
  • [5] Chemical transformation of the electrode surface of lithium-ion battery after storing at high temperature
    Araki, K
    Sato, N
    [J]. JOURNAL OF POWER SOURCES, 2003, 124 (01) : 124 - 132
  • [6] Failure and stabilization mechanisms of graphite electrodes
    Aurbach, D
    Levi, MD
    Levi, E
    Schechter, A
    [J]. JOURNAL OF PHYSICAL CHEMISTRY B, 1997, 101 (12): : 2195 - 2206
  • [7] THE APPLICATION OF EQCM TO THE STUDY OF THE ELECTROCHEMICAL-BEHAVIOR OF PROPYLENE CARBONATE SOLUTIONS
    AURBACH, D
    ZABAN, A
    [J]. JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 1995, 393 (1-2): : 43 - 53
  • [8] A hybrid activated carbon-manganese dioxide capacitor using a mild aqueous electrolyte
    Brousse, T
    Toupin, M
    Bélanger, D
    [J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2004, 151 (04) : A614 - A622
  • [9] TiO2 (B)/activated carbon non-aqueous hybrid system for energy storage
    Brousse, Thierry
    Marchand, Rene
    Taberna, Pierre-Louis
    Simon, Patrice
    [J]. JOURNAL OF POWER SOURCES, 2006, 158 (01) : 571 - 577
  • [10] Tantalum oxide-ruthenium oxide hybrid(R) capacitors
    Chang, TY
    Wang, X
    Evans, DA
    Robinson, SL
    Zheng, JP
    [J]. JOURNAL OF POWER SOURCES, 2002, 110 (01) : 138 - 143