Neutron scattering studies of superconducting MgB2 tapes

The capability of manufacturing long superconducting MgB2 wires with already remarkable critical currents makes this material a very promising candidate for future applications. Tapes are prepared by the powder-in-tube technique. After the cold working procedure typically carried out by wire drawing and cold rolling, it has been found that a final sintering step carried out in argon atmosphere is a key process for further improving the superconducting properties of the conductors. To study the effect of the deformation and heat treatment processes, we performed neutron scattering experiment. Due to the high penetration depth of neutron inside matter, it was possible to analyse the MgB2 phase still wrapped in the Ni sheath. Our studies were carried out by a full spectra refinement by the Rietveld method. In the starting superconducting powder a large Mg deficiency was observed. In the tapes we found that the large forces applied during the cold working induced a large MgB2 lattice deformation, and that it is partly relaxed during the final sintering process. An important correlation of the residual stress with the critical temperature and the pinning properties was pointed out. We also observed the appearance of detrimental secondary phases during the sintering process. In particular, the MgB2 phase reacted with the nickel sheath and MgB2Ni2.5 was formed at temperatures higher than 850 degreesC. These results are of basic importance for a further optimization of the transport properties at moderate fields where applications of MgB2 tapes are already envisageable.