Nanocrystalline iron oxide aerogels as mesoporous magnetic architectures

被引:160
作者
Long, JW
Logan, MS
Rhodes, CP
Carpenter, EE
Stroud, RM
Rolison, DR
机构
[1] USN, Res Lab, Surface Chem Branch, Washington, DC 20375 USA
[2] USN, Res Lab, Mat & Sensors Branch, Washington, DC 20375 USA
关键词
D O I
10.1021/ja046044f
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
We have developed crystalline nanoarchitectures of iron oxide that exhibit superpararnagne behavior while still retaining the desirable bicontinuous pore-solid networks and monolithic nature of an aerogel. Iron oxide aerogels are initially produced in an X-ray-amorphous. high-surface-area loan. by adapting recently established sol-gel methods using Fe(III) salts and epoxide-based proton scavengers. Controlled temperature/atmosphere treatments convert the as-prepared iron oxide aerocals into nanocrystalline forms with the inverse spinel structure. As a function of the bathing gas, treatment lamp temerature and treatment history, these nanocrystalline forms can be reversibly tuned to predominantly exhibit either Fe3O4 (magnetite) or gamma-Fe2O3 (maghemite) phases, as verified by electron microscopy, X-ray am electron. diffraction, microprobe Raman spectroscopy, and magnetic analysis. Peak deconvolution oil the Raman-active bands yields valuable information on the local structure and vacancy content of the various aerogel forms, and facilitates the differentiation of Fe3O4 and gamma-Fe2O3 components. which are difficult to assign using only diffraction methods. These nanocrystalline, magnetic forms retain the inherent characteristics of aerogels, including high surface area (>140 m(2) g(-1)) through-connected porosity concentrated in the mesopore size range (2-50 rim), and nanoscale particle sizes (7-18 nm). On the basis of this synthetic and processing protocol, we produce multifunctional nanostructured material with effective control of the pore-solid architecture, the nanocrystalline phase. and subsequent magnetic properties.
引用
收藏
页码:16879 / 16889
页数:11
相关论文
共 91 条
[1]   Enhancing the activity of fuel-cell reactions by designing three-dimensional nanostructured architectures: Catalyst-modified carbon-silica composite aerogels (vol 2, pg 239, 2002) [J].
Anderson, ML ;
Stroud, RM ;
Rolison, DR .
NANO LETTERS, 2003, 3 (09) :1321-1321
[2]  
Anderson ML, 2002, NANO LETT, V2, P235, DOI 10.1021/n1015707d
[3]   Au/α-Fe2O3 catalyst for water-gas shift reaction prepared by deposition-precipitation [J].
Andreeva, D ;
Tabakova, T ;
Idakiev, V ;
Christov, P ;
Giovanoli, R .
APPLIED CATALYSIS A-GENERAL, 1998, 169 (01) :9-14
[4]   Influence of grain size, oxygen stoichiometry, and synthesis conditions on the γ-Fe2O3 vacancies ordering and lattice parameters [J].
Belin, T ;
Guigue-Millot, N ;
Caillot, T ;
Aymes, D ;
Niepce, JC .
JOURNAL OF SOLID STATE CHEMISTRY, 2002, 163 (02) :459-465
[5]   INFLUENCE OF CRYSTALLITE SIZE ON MAGNETIC PROPERTIES OF ACICULAR GAMMA-FE2O3 PARTICLES [J].
BERKOWIT.AE ;
SCHUELE, WJ ;
FLANDERS, PJ .
JOURNAL OF APPLIED PHYSICS, 1968, 39 (2P2) :1261-&
[6]  
Bersani D, 1999, J RAMAN SPECTROSC, V30, P355, DOI 10.1002/(SICI)1097-4555(199905)30:5<355::AID-JRS398>3.0.CO
[7]  
2-C
[8]   The structure of the spinel group of crystals. [J].
Bragg, W. H. .
PHILOSOPHICAL MAGAZINE, 1915, 30 (175-80) :305-315
[9]   Magnetic behaviour of iron oxide nanoparticles dispersed in a silica matrix [J].
Caizer, C ;
Savii, C ;
Popovici, M .
MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 2003, 97 (02) :129-134
[10]   Superparamagnetic behaviour of γ-Fe2O3 nanoparticles dispersed in a silica matrix [J].
Cannas, C ;
Concas, G ;
Gatteschi, D ;
Falqui, A ;
Musinu, A ;
Piccaluga, G ;
Sangregorio, C ;
Spano, G .
PHYSICAL CHEMISTRY CHEMICAL PHYSICS, 2001, 3 (05) :832-838