High coercivity in SiO2-doped CoFe2O4 powders and thin films

被引：66

作者：

Ding, J ^{[1
]}

Chen, YJ ^{[1
]}

Shi, Y ^{[1
]}

Wang, S ^{[1
]}

机构：

[1] Natl Univ Singapore, Dept Mat Sci, Singapore 119260, Singapore

来源：

APPLIED PHYSICS LETTERS | 2000年 / 77卷 / 22期

关键词：

D O I：

10.1063/1.1328374

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

Mossbauer and magnetic studies have shown that 1-2 wt % of SiO2 could be dissolved in the CoFe2O4 structure. Changes in magnetization and Curie temperature were observed. The presence of SiO2 might enhance magnetic anisotropy. Coercivity values of up to 3.5 kOe were measured for mechanically alloyed CoFe2O4/SiO2 powders. High coercivities were also achieved in SiO2-doped Co-ferrite thin films prepared by sputtering technique. The Co-ferrite thin film deposited on a silicon wafer using a 5 wt % SiO2/Co-ferrite target possessed a coercivity of 7.4 kOe. Spring-magnet behavior was observed, indicating the possible presence of remanence enhancement due to exchange coupling because of nanocrystalline structure. (C) 2000 American Institute of Physics. [S0003-6951(00)01348-6].

引用

页码：3621 / 3623

页数：3

共 14 条

[1] Microstructure, magnetic, and magneto-optical properties of chemical synthesized Co-RE (RE=Ho, Er, Tm, Yb, Lu) ferrite nanocrystalline films [J].

Cheng, FX ;

Jia, JT ;

Xu, ZG ;

Zhou, B ;

Liao, CS ;

Yan, CH ;

Chen, LY ;

Zhao, HB .

JOURNAL OF APPLIED PHYSICS, 1999, 86 (05) :2727-2732

[2] High-coercivity ferrite magnets prepared by mechanical alloying [J].

Ding, J ;

Miao, WF ;

McCormick, PG ;

Street, R .

JOURNAL OF ALLOYS AND COMPOUNDS, 1998, 281 (01) :32-36

[3] HIGH MAGNETIC PERFORMANCE IN MECHANICALLY ALLOYED CO-SUBSTITUTED FE3O4 [J].

DING, J ;

REYNOLDS, T ;

MIAO, WF ;

MCCORMICK, PG ;

STREET, R .

APPLIED PHYSICS LETTERS, 1994, 65 (24) :3135-3136

[4]

DING J, RECENT RES DEV MAT S, V1, P15

[5]

DING J, 1995, SOLID STATE COMMUN, V95, P102

[6] A consistent interpretation of the magneto-optical spectra of spinel type ferrites (invited) [J].

Fontijn, WFJ ;

van der Zaag, PJ ;

Feiner, LF ;

Metselaar, R ;

Devillers, MAC .

JOURNAL OF APPLIED PHYSICS, 1999, 85 (08) :5100-5105

[7]

GREENWOOD NN, 1971, MOSSBAUER SPECTROSCO, P239

[8]

HAPMORICH J, 1985, J APPL PHYS, V57, P3581

[9] Co ferrite films with excellent perpendicular magnetic anisotropy and high coercivity deposited at low temperature [J].

Kitamoto, Y ;

Kantake, S ;

Shirasaki, F ;

Abe, M ;

Naoe, M .

JOURNAL OF APPLIED PHYSICS, 1999, 85 (08) :4708-4710

[10] THE EXCHANGE-SPRING MAGNET - A NEW MATERIAL PRINCIPLE FOR PERMANENT-MAGNETS [J].

KNELLER, EF ;

HAWIG, R .

IEEE TRANSACTIONS ON MAGNETICS, 1991, 27 (04) :3588-3600

← 1 2 →