Fabrication and oxidation behavior of LaB6-ZrB2 composites

被引：28

作者：

Gao, RL ^{[1
]}

Min, GH ^{[1
]}

Yu, HS ^{[1
]}

Zheng, SQ ^{[1
]}

Lu, QL ^{[1
]}

Han, HD ^{[1
]}

Wang, WT ^{[1
]}

机构：

[1] Shandong Univ, Sch Mat Sci & Engn, Jinan 250061, Peoples R China

来源：

CERAMICS INTERNATIONAL | 2005年 / 31卷 / 01期

关键词：

hot pressing; sintering; LaB6-ZrB2; composites; oxidation behaviors;

D O I：

10.1016/j.ceramint.2004.02.006

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

LaB6-ZrB2 cutectic composites were sintered by hot pressing. The oxidation behavior of LaB6-ZrB2 entectic composites was studied in the temperature range of 600-1300degreesC. It was shown that the sample weight increased with increasing oxidation temperature and prolonging holding time. The rate of weight change was described by k(p) = 6.24 x 10(-4) exp(-38, 940/RD g(2)/m(2) s, but it changed according to the change of oxidation time at 1200degreesC. Weight gain was evident in less than 1h, but it slowed down Subsequently due to the evaporation of B2O3. The rate of weight change increased abruptly at 1300degreesC. The oxidation resistance of LaB6-ZrB2 composites was higher than that of monolithic LaB6. (C) 2004 Elsevier Ltd and Techna S.r.l. All rights reserved.

引用

页码：15 / 19

页数：5

共 7 条

[1]

CHEN CM, 1997, THESIS NW POLYTECHNI

[2]

Lin Zulun, 1997, High Power Laser and Particle Beams, V9, P591

[3]

MUSHIAKI M, 1993, MAT SCI ENG A-STRUCT, V163, P177, DOI 10.1016/0921-5093(93)90785-D

[4] Field electron emission from LaB6 and TiN emitter arrays fabricated by transfer mold technique [J].

Nakamoto, M ;

Fukuda, K .

APPLIED SURFACE SCIENCE, 2002, 202 (3-4) :289-294

[5] MICROMECHANICAL PROPERTIES OF MELTED BORIDES OF RARE-EARTH METALS [J].

PADERNO, VN ;

PADERNO, YB ;

PILYANKEVICH, AN ;

LAZORENKO, VI ;

BULYCHEV, SI .

JOURNAL OF THE LESS-COMMON METALS, 1979, 67 (02) :431-436

[6]

Paderno Y.U., 1990, AIP C P, V231, P561

[7] OXYGEN-ENHANCED THERMIONIC EMISSION PATTERN OF HEMISPHERICAL SINGLE-CRYSTAL LAB6 [J].

SHIMIZU, R ;

ONODA, H ;

HASHIMOTO, H ;

HAGIWARA, H .

JOURNAL OF APPLIED PHYSICS, 1984, 55 (05) :1379-1387

← 1 →