Analysis of the conductivity of commercial easy sintering grade 3 mol% Y2O3-ZrO2 materials

Fine grain zirconia-yttria materials are required for enhanced performance in solid oxide fuel cells and related devices and in applications requiring good thermo-mechanical properties. Materials with about 3 mol% Y2O3-ZrO2 composition are good electrolyte materials for solid oxide fuel cell, ceramic membrane oxygen separation and a number of related devices because of their superior mechanical properties and ease of fabrication into thin self-supporting structures in comparison with a material in the 8-10 mol% Y2O3-ZrO2 composition range. In this study, sintering behaviour, impedance studies, four-probe DC conductivity measurements and microstructure analysis has been performed on various easy sintering grade materials from two commercial powder suppliers. These materials achieve near theoretical density at sintering temperatures as low as 1350-1400 degreesC. For direct comparison of the conductivity and impedance behaviour in easy sintering grade materials, several other 3 mol% Y2O3-ZrO2 powders were also investigated. The total ionic conductivity at 850 degreesC in easy sintering grade materials is comparable with normal-grade commercial materials of similar composition despite a slightly higher grain boundary impedance at lower temperatures (below similar to450 degreesC). There were no obvious differences in the grain boundary thickness, calculated from the impedance data, of normal and easy sintering grade materials. (C) 2004 Elsevier B.V. All rights reserved.