Critical currents of OCMG processed Nd123 crystals

被引：28

作者：

Higuchi, T ^{[1
]}

Yoo, SI ^{[1
]}

Sawada, K ^{[1
]}

Sakai, N ^{[1
]}

Murakami, M ^{[1
]}

机构：

[1] SUPERCONDUCT RES LAB,MINATO KU,TOKYO 105,JAPAN

来源：

PHYSICA C | 1996年 / 263卷 / 1-4期

关键词：

D O I：

10.1016/0921-4534(96)00154-2

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

Critical current densities of Nd123 crystals flux grown by the oxygen-controlled-melt-growth (OCMG) process have been studied with DC magnetization measurements, The superconducting transition temperature (T-c) of the Nd123 crystal flux grown in 0.1%O-2-Ar gas was 94 K with the applied field of 10 Oe parallel to the c-axis. The sample was found to be homogeneous without weakly linked regions through magneto-optical measurements. DC magnetization-hysteresis curves measured with a SQUID magnetometer exhibited a peak effect at various temperatures above 70 K. The peak effect is attributable to field-induced pinning by finely distributed low-T-c phases. The sample exhibited high critical current density (J(c)) values of 4 x 10(4) A/cm(2) in 2 T and over 1 X 10(4) A/cm(2) in 4 T at 77 K for Fields parallel to the c-axis.

引用

页码：396 / 400

页数：5

共 10 条

[1]

DAUEMLING M, 1990, NATURE, V346, P332

[2] HIGH CRITICAL-CURRENT DENSITY OF ND(BA,ND)(2)CU3O7-DELTA SINGLE-CRYSTALS [J].