Dense YSZ electrolyte films prepared by modified electrostatic powder coating

被引：16

作者：

Bao, WT ^{[1
]}

Zhu, W ^{[1
]}

Zhu, GY ^{[1
]}

Gao, JF ^{[1
]}

Meng, GY ^{[1
]}

机构：

[1] Univ Sci & Technol China, Dept Mat Sci & Engn, Hefei 230026, Peoples R China

来源：

SOLID STATE IONICS | 2005年 / 176卷 / 7-8期

基金：

中国国家自然科学基金;

关键词：

electrostatic powder coating; dense electrolyte film; YSZ; SOFCs;

D O I：

10.1016/j.ssi.2004.10.023

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

A dense yttria-stabilized zirconia (YSZ, 8 mol% Y2O3) film was successfully fabricated by an electrostatic powder-coating process associated with suspension modifying on a porous anode (NiO/YSZ) substrate. The YSZ green powder layer formed by the unmodified process consisted of the loosely packed particles and could not be densified by sintering. After modifying this green layer by a suspension, a dense wet layer was formed that could be sintered at 1450 degreesC. SEM observations showed the film to be dense and approximately 8 mum thick. A single cell with this YSZ electrolyte on Ni/YSZ anode and Ag as cathode was assembled and tested in the temperature range from 550 to 750 degreesC. The open circuit voltage (OCV) and peak power density of the single cell at 750 degreesC was 1.1 V, which is very close to the theoretical value, and 142 mW/cm(2), respectively. The results illustrate that YSZ membranes fabricated by this process are quite dense and gas tight. (C) 2004 Elsevier B.V. All rights reserved.

引用

页码：669 / 674

页数：6

共 16 条

[1] Solid oxide electrolyte fuel cell review [J].

Badwal, SPS ;

Foger, K .

CERAMICS INTERNATIONAL, 1996, 22 (03) :257-265

[2] The science and technology of electrostatic powder spraying, transport and coating [J].

Bailey, AG .

JOURNAL OF ELECTROSTATICS, 1998, 45 (02) :85-120

[3] Adhesion of charged powders to a metal surface in the powder coating process [J].

Banerjee, S ;

Mazumder, MK .

IEEE TRANSACTIONS ON INDUSTRY APPLICATIONS, 1996, 32 (06) :1243-1249

[4] Supported Zr(Sc)O2 SOFCs for reduced temperature prepared by slurry coating and co-firing [J].

Cai, Z ;

Lan, TN ;

Wang, S ;

Dokiya, M .

SOLID STATE IONICS, 2002, 152 :583-590

[5] Chemical vapour deposition of coatings [J].

Choy, KL .

PROGRESS IN MATERIALS SCIENCE, 2003, 48 (02) :57-170

[6] PROCESSING OF PORCELAIN ENAMEL GLASS POWDERS FOR ELECTROSTATIC SPRAYING [J].

FU, DC .

POWDER TECHNOLOGY, 1995, 85 (01) :65-69

[7] Performance of intermediate temperature solid oxide fuel cells with La(Sr)Ga(Mg)O3 electrolyte film [J].

Fukui, T ;

Ohara, S ;

Murata, K ;

Yoshida, H ;

Miura, K ;

Inagaki, T .

JOURNAL OF POWER SOURCES, 2002, 106 (1-2) :142-145

[8] Ceria-based solid electrolytes - Review [J].

Inaba, H ;

Tagawa, H .

SOLID STATE IONICS, 1996, 83 (1-2) :1-16

[9] Study on the properties of YSZ electrolyte made by plaster casting method and the applications in solid oxide fuel cells [J].

Liu, J ;

Liu, W ;

Lu, Z ;

Pei, L ;

Jia, L ;

He, LY ;

Su, WH .

SOLID STATE IONICS, 1999, 118 (1-2) :67-72

[10] Characterization of solid oxide fuel cell device having a three-layer film structure grown by RF magnetron sputtering [J].

Nagata, A ;

Okayama, H .

VACUUM, 2002, 66 (3-4) :523-529

← 1 2 →