Synthesis of highly porous yttria-stabilized zirconia by tape-casting methods

被引:202
作者
Boaro, M [1 ]
Vohs, JM [1 ]
Gorte, RJ [1 ]
机构
[1] Univ Penn, Dept Chem & Biomol Engn, Philadelphia, PA 19104 USA
关键词
D O I
10.1111/j.1151-2916.2003.tb03311.x
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Porous ceramics of Y2O3-stabilized ZrO2 (YSZ) were prepared by tape-casting methods using both pyrolyzable pore formers and NiO followed by acid leaching. The porosity of YSZ wafers increased in a regular manner with the mass of graphite or polymethyl methacrylate (PMMA) to between 60% and 75% porosity. SEM indicated that the shape of the pores in the final ceramic was related to the shape of the pore formers, so that the pore size and microstructure of YSZ wafers could be controlled by the choice of pore former. Dilatometry measurements showed that measurable shrinkage started at 1300 K, and a total shrinkage of 26% was observed, independent of the amount or type of pore former used. Temperature-programmed oxidation (TPO) measurements on the green tapes demonstrated that the binders and dispersants were combusted between 550 and 750 K, that PMMA decomposed to methyl methacrylate between 500 and 700 K, and that graphite combusted above 900 K. The porosity of YSZ ceramics prepared by acid leaching of nickel from NiO-YSZ, with 50 wt% NiO, was studied as a function of NiO and YSZ particle size. Significant changes in pore dimension were found when NiO particle size was changed.
引用
收藏
页码:395 / 400
页数:6
相关论文
共 30 条
[1]  
[Anonymous], 1998, POROUS MAT PROCESS T
[2]   Structure/performance relations for Ni/yttria-stabilized zirconia anodes for solid oxide fuel cells [J].
Brown, M ;
Primdahl, S ;
Mogensen, M .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2000, 147 (02) :475-485
[3]   Water-based tape casting and manufacturing of laminated structures [J].
Carlström, E ;
Kristoffersson, A .
EURO CERAMICS VII, PT 1-3, 2002, 206-2 :205-210
[4]   Ceramic foams: fabrication, properties and applications [J].
Colombo, P .
EURO CERAMICS VII, PT 1-3, 2002, 206-2 :1913-1918
[5]   Engineered porosity via tape casting, lamination and the percolation of pyrolyzable particulates [J].
Corbin, SF ;
Apté, PS .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1999, 82 (07) :1693-1701
[6]   Influence of green formulation and pyrolyzable particulates on the porous microstructure and sintering characteristics of tape cast ceramics [J].
Corbin, SF ;
Lee, J ;
Qiao, X .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2001, 84 (01) :41-47
[7]   A novel method for preparing anode cermets for solid oxide fuel cells [J].
Craciun, R ;
Park, S ;
Gorte, RJ ;
Vohs, JM ;
Wang, C ;
Worrell, WL .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1999, 146 (11) :4019-4022
[8]  
Davis JB, 2000, J AM CERAM SOC, V83, P2369, DOI 10.1111/j.1151-2916.2000.tb01563.x
[9]   CONDUCTIVITY OF POROUS NI/ZRO2-Y2O3 CERMETS [J].
DEES, DW ;
CLAAR, TD ;
EASLER, TE ;
FEE, DC ;
MRAZEK, FC .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1987, 134 (09) :2141-2146
[10]   Synthesis of porous ceramics with complex pore structure by freeze-dry processing [J].
Fukasawa, T ;
Ando, M ;
Ohji, T ;
Kanzaki, S .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2001, 84 (01) :230-232