High packing density of Zr- and Pd-based bulk amorphous alloys

被引:142
作者
Inoue, A [1 ]
Negishi, T
Kimura, HM
Zhang, T
Yavari, AR
机构
[1] Tohoku Univ, Inst Mat Res, Sendai, Miyagi 9808577, Japan
[2] CNRS, LTPCM, F-38402 Grenoble, France
[3] Inst Natl Polytech, F-38402 Grenoble, France
来源
MATERIALS TRANSACTIONS JIM | 1998年 / 39卷 / 02期
关键词
bulk amorphous alloy; zirconium base alloy; palladium base alloy; density; packing density; atomic configuration; glass-forming ability;
D O I
10.2320/matertrans1989.39.318
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
With the aim of evaluating a packing density of the new bulk amorphous alloys, the densities of bulk Zr60Al10Cu30, Zr55Al10Cu30Ni5 and Pd40Cu30Ni10P20 alloys were measured in cast amorphous and annealing-induced crystallized states. The densities of the as-cast amorphous and crystallized phases were measured to be respectively 6.72 and 6.74 Mg/m(3) for the Zr-Al-Cu alloy, 6.82 and 6.85 Mg/m(3) for the Zr-Al-Cu-Ni alloy, 9.27 and 9.31 Mg/m(3) for the Pd-Cu-Ni-P alloy. The annealing leading to the fully relaxed amorphous state induced slight increases of density to 6.83 Mg/m(3) for the latter Zr-based alloy and to 9.28 Mg/m(3) for the Pd-based alloy. The increase in density due to crystallization is evaluated to be in the range of 0.30 to 0.54% which is much smaller than that (2 to 3%) for the previously reported amorphous alloys. This result indicates that the new bulk amorphous alloys have more packed atomic configurations than ordinary amorphous alloys which require high cooling rates above 10(4) K/s for glass formation. It is therefore thought that the higher packing density achieves the high glass-forming ability through the decrease of atomic diffusivity and the increase of viscosity. The present information obtained from the density data is consistent with the previously proposed concept for the achievement of high glass-forming ability for multicomponent amorphous alloys.
引用
收藏
页码:318 / 321
页数:4
相关论文
共 27 条
  • [1] GLASSY METALS
    CHEN, HS
    [J]. REPORTS ON PROGRESS IN PHYSICS, 1980, 43 (04) : 353 - +
  • [2] MG-NI-LA AMORPHOUS-ALLOYS WITH A WIDE SUPERCOOLED LIQUID REGION
    INOUE, A
    KOHINATA, M
    TSAI, AP
    MASUMOTO, T
    [J]. MATERIALS TRANSACTIONS JIM, 1989, 30 (05): : 378 - 381
  • [3] AL-LA-CU AMORPHOUS-ALLOYS WITH A WIDE SUPERCOOLED LIQUID REGION
    INOUE, A
    YAMAGUCHI, H
    ZHANG, T
    MASUMOTO, T
    [J]. MATERIALS TRANSACTIONS JIM, 1990, 31 (02): : 104 - 109
  • [4] Inoue A, 1996, SCI REP RES TOHOKU A, V42, P1
  • [5] Multicomponent Co-based amorphous alloys with wide supercooled liquid region
    Inoue, A
    Katsuya, A
    [J]. MATERIALS TRANSACTIONS JIM, 1996, 37 (06): : 1332 - 1336
  • [6] NEW AMORPHOUS MG-CE-NI ALLOYS WITH HIGH-STRENGTH AND GOOD DUCTILITY
    INOUE, A
    OHTERA, K
    KITA, K
    MASUMOTO, T
    [J]. JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1988, 27 (12): : L2248 - L2251
  • [7] New Fe-Co-Ni-Zr-B amorphous alloys with wide supercooled liquid regions and good soft magnetic properties
    Inoue, A
    Zhang, T
    Itoi, T
    Takeuchi, A
    [J]. MATERIALS TRANSACTIONS JIM, 1997, 38 (04): : 359 - 362
  • [8] AL-LA-NI AMORPHOUS-ALLOYS WITH A WIDE SUPERCOOLED LIQUID REGION
    INOUE, A
    ZHANG, T
    MASUMOTO, T
    [J]. MATERIALS TRANSACTIONS JIM, 1989, 30 (12): : 965 - 972
  • [9] FE-BASED FERROMAGNETIC GLASSY ALLOYS WITH WIDE SUPERCOOLED LIQUID REGION
    INOUE, A
    GOOK, JS
    [J]. MATERIALS TRANSACTIONS JIM, 1995, 36 (09): : 1180 - 1183
  • [10] HIGH-STRENGTH BULK AMORPHOUS-ALLOYS WITH LOW CRITICAL COOLING RATES
    INOUE, A
    [J]. MATERIALS TRANSACTIONS JIM, 1995, 36 (07): : 866 - 875