Characterisation of electrodeposited nanocrystaltine Ni-Mo alloys

Ni-Mo nanocrystalline layers were electrodeposited using direct current from citrate-ammonia solutions. The quartz crystal microbalance investigation confirms that the discharge process starts with hydrogen evolution before the onset of the alloy deposition. The grain size was estimated from X-ray line broadening. It decreases when the molybdenum content is increased. It is smaller for layers deposited at pH 9.5 than 8.5. The microhardness exhibits a maximum close to 800 Vickers for tau(MO) around 17 wt%. For higher tau(MO) a softening is observed showing a deviation from Hall-Petch behaviour due to small grain size. In deaerated hydrochloric solutions, the layers show a large passivation domain without any pitting. The corrosion currents as well as the passivation currents, higher than for the bulk Hastelloy B alloy, decrease when tau(MO) is increased.