Isothermal crystallization behavior of isotactic polypropylene blended with small loading of polyhedral oligomeric silsesquioxane

The isothermal crystallization kinetics and morphology development of isotactic polypropylene (iPP) blended with small loading of nanostructure of polyhedral oligomeric silsesquioxane (POSS) were studied with differential scanning calorimetry (DSC), polarized optical microscopy (POM), and wide-angle X-ray diffraction (WAXD). The crystallization behaviors of iPP/POSS composites presented an unusual crystallization behavior during isothermal and nonisothermal crystallization conditions. The exothermic morphologies of isothermal and nonisothermal crystallization of iPP/POSS composites changed remarkably with increasing POSS. Moreover, the developments of spherulitic morphology for iPP/POSS composites showed that the major dispersed POSS molecules became nanocrystals first and then aggregated together forming thread- or network-like morphologies, respectively, depending on POSS content, which was observed. It implies that these major POSS nanocrystals' morphologies appeared as an effective nucleating agent and promoted the nucleation rate of iPP, whereas the minor dispersed POSS molecules that had slight miscibility between iPP retarded the nucleation and growth rates of iPP in the remaining bulk region. Therefore, the isothermal crystallization showed a single exothermic peak at pure iPP and POSS-1.0, whereas at POSS-2.0 and POSS-3.0, displayed the multi-exothermic peaks during isothermal crystallization. These faces indicated that POSS molecules were both influence on the transport of iPP chain in the melted state and on the free-energy of formation the critical nuclei of iPP assisted by the POSS structures were observed. Therefore, we postulated that the crystallization mechanisms of multi-exothermic peaks in isothermal crystallization may proceed to combine the "nucleating agent inducing nucleation of iPP event assisted by the POSS domains" that the nucleation of iPP does occur preferentially on the surfaces of the POSS "threads" or "networks" structures, and "nucleation and growth of iPP in the remaining bulk melted iPP region retarded by dispersed POSS molecules". Therefore, effects of POSS content on the isothermal and nonisothermal crystallization behaviors of iPP/POSS composites due to the POSS molecules partially miscible with iPP, at very small loading of POSS molecules, promoted or retarded the rates of nucleation and growth of iPP depending on the POSS content and crystallization temperature were discussed. (c) 2007 Elsevier Ltd. All rights reserved.