Effect of prealuminizing diffusion treatment on microstructural evolution of high-activity Pt-aluminide coatings

被引:46
作者
Das, DK
Singh, V
Joshi, SV
机构
[1] Def Met Res Lab, Hyderabad 500058, Andhra Pradesh, India
[2] Banaras Hindu Univ, Dept Met Engn, Varanasi 221005, Uttar Pradesh, India
来源
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2000年 / 31卷 / 08期
关键词
D O I
10.1007/s11661-000-0231-y
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The effect of prealuminizing (or prior) diffusion treatment on the evolution of Pt-aluminide coatings on the Ni-based superalloy CM-247 has been studied by using a single-step, high-activity aluminizing process, Coatings generated without any prior diffusion treatment, as well as those formed by adopting two extreme prior-diffusion schedules (at 850 degrees C for 0.5 hours and at 1034 degrees C for 5 hours), were investigated by analyzing the coating structures at various stages of aluminizing. When the dilution of the Pt layer, caused by its interdiffusion with the substrate during the prior diffusion treatment, is only marginal (as in the case of no prior diffusion and diffusion at 850 degrees C for 0.5 hours), the equilibrium Pt-aluminide coating structure evolves through the formation of two transient layers during the initial stages of aluminizing, In contrast, for diffusion at 1034 degrees C for 5 hours, which results in extensive dilution of the Pt layer, the two-phase equilibrium structure (PtAl2 in a matrix of NiAl) in the outer layer of the coating is found to develop during very early stages of aluminizing and remains unchanged, even over extended periods of aluminizing. Further, in the case of prior diffusion at 1034 degrees C for 5 hours, Pt is found to remain distributed to a greater extent over the entire thickness of the coating than in the cases of limited prior diffusion treatment. The present findings underline the significance of the nature of the prior-diffusion schedule on the microstructural evolution of Pt-aluminide coatings. It has also been found that a prealuminizing diffusion treatment is particularly important for Pt-aluminide coatings from the point of view of coating adhesion to the substrate.
引用
收藏
页码:2037 / 2047
页数:11
相关论文
共 23 条
[1]   INFLUENCE OF SMALL PT ADDITIONS ON AL2O3 SCALE ADHERENCE [J].
ALLAM, IM ;
AKUEZUE, HC ;
WHITTLE, DP .
OXIDATION OF METALS, 1980, 14 (06) :517-530
[2]  
BAUR R, 1985, HIGH TEMP TECHNOL, V3, P59
[3]   Evolution of aluminide coating microstructure on nickel-base cast superalloy CM-247 in a single-step high-activity aluminizing process [J].
Das, DK ;
Singh, V ;
Joshi, SV .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (08) :2173-2188
[4]  
DK Das, 1996, 96206 DMRL TR
[5]   STRUCTURE AND 700-DEGREES-C HOT CORROSION BEHAVIOR OF CHROMIUM MODIFIED PLATINUM ALUMINIDE COATINGS [J].
DUST, M ;
DEB, P ;
BOONE, DH ;
SHANKAR, S .
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1986, 4 (06) :2571-2576
[6]   DEVELOPMENT, GROWTH, AND ADHESION OF AL2O3 ON PLATINUM-ALUMINUM ALLOYS [J].
FELTEN, EJ ;
PETTIT, FS .
OXIDATION OF METALS, 1976, 10 (03) :189-223
[7]   Mechanism of spallation in platinum aluminide/electron beam physical vapor-deposited thermal barrier coatings [J].
Gell, M ;
Vaidyanathan, K ;
Barber, B ;
Cheng, J ;
Jordan, E .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1999, 30 (02) :427-435
[8]   MECHANISMS OF FORMATION OF DIFFUSION ALUMINIDE COATINGS ON NICKEL-BASE SUPERALLOYS [J].
GOWARD, GW ;
BOONE, DH .
OXIDATION OF METALS, 1971, 3 (05) :475-&
[9]   ALUMINIZATION OF PLATINUM AND PLATINUM-COATED IN-738 [J].
JACKSON, MR ;
RAIRDEN, JR .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1977, 8 (11) :1697-1707
[10]  
KAUFMAN L, 1975, METALL TRANS A, V6, P2123, DOI 10.1007/BF03161839