Thermal and chemical properties of diopside-wollastonite glass-ceramics in the SiO2-CaO-MgO system from raw materials

被引：73

作者：

Abdel-Hameed, SAM ^{[1
]}

El-Kheshen, AA ^{[1
]}

机构：

[1] Natl Res Ctr, Glass Res Dept, Cairo 12622, Egypt

来源：

CERAMICS INTERNATIONAL | 2003年 / 29卷 / 03期

关键词：

thermal properties; chemical properties; glass ceramics; SiO2-CaO-MgO system;

D O I：

10.1016/S0272-8842(02)00114-1

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The crystallization process of ternary system SiO2-CaO-MgO from waste raw materials was investigated by DTA and polarizing microscope and characterized by chemical durability for glasses and glass-ceramics. The effects of compositional changes on bulk crystallization and growth morphology were also studied. beta-wollastonite and diopside, were identified after heat-treatment. The coarse grained morphology with directional surface crystallization was observed. Studying of chemical durability shows that, the weight loss increased by increasing CaO content on the expense of MgO in both acidic or alkaline solution. (C) 2002 Elsevier Science Ltd and Techna S.r.l. All rights reserved.

引用

页码：265 / 269

页数：5

共 11 条

[1]

ABDELHAMEED SAM, 1995, THESIS ZAGAZIG U EGY

[2]

[Anonymous], 1982, CHEM GLASSES

[3]

[Anonymous], J ENG SCI

[4] Thermodynamic investigation of crystallization behaviour of pyroxenic basalt-based glasses [J].

El-Shennawi, AWA ;

Morsi, MM ;

Khater, GA ;

Abdel-Hameed, SAM .

JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY, 1998, 51 (02) :553-560

[5]

KARAMANOV A, 1990, Patent No. 50879

[6]

LEWINS J, 1965, THESIS SHEFFIELD

[7]

McMillan P.W., 1979, Glass-Ceramic, Vsecond

[8]

NAKAMURA S, 1976, Patent No. 3955989

[9]

STRND Z, 1986, GLASS CERAMIC MAT

[10]

WATANABLE K, 1993, J NON-CRYST SOLIDS, V169, P306

← 1 2 →