Dynamic recrystallization behavior of 35CrMo structural steel

被引:22
作者
Zhang, B [1 ]
Zhang, HB
Ruan, XY
机构
[1] Shanghai Jiao Tong Univ, Dept Plastic Forming Engn, Shanghai 200030, Peoples R China
[2] Inst Shanghai Technol, Dept Mat Engn, Shanghai 20035, Peoples R China
来源
JOURNAL OF CENTRAL SOUTH UNIVERSITY OF TECHNOLOGY | 2003年 / 10卷 / 01期
基金
中国国家自然科学基金;
关键词
dynamic recrystallization; 0-epsilon curve; recrystallizaiton kinetics; initial grain size;
D O I
10.1007/s11771-003-0063-1
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
The dynamic recrystallization behavior of 35CrMo steel was studied with compression test in the temperature range of 1 223-1 423 K and the strain rate range of 0.01-10.00 s(-1). The initiation and evolution of dynamic recrystallization were investigated with microstructure analysis and then the critical strain E, for dynamic recrystallization initiation, the strain for maximum softening rate epsilon(*) and the steady strain E. were obtained to be 2.92X10(-3)Z(0.1381), 1.60X10(-3)Z(0.1780) and 3.26X10(-2)XZ(0.0972) respectively by analysis of work-hardening rate-strain 04 curves, where Z is the Zener-Hollomon parameter. The dynamic recrystallization fraction was determined using recrystallization theory, and the effects of initial grain size, strain rate and deformated temperature on the dynamic recrystallization kinetics were investigated. The results show: X-DRX = 1 - exp(-3.23( epsilon-epsilon(c)/epsilon(s)-epsilon(c))2.28), the dynamic recrystallization fraction is slightly delayed due to the es -cc somewhat larger initial grain size and markedly delayed with the decrease of temperature. On the other hand, it is significantly accelerated with the increase of the strain rate. Finally the relationships between the initiation time, ending time of dynamic recrystallization and the deformed temperature were analyzed in detail.
引用
收藏
页码:13 / 19
页数:7
相关论文
共 11 条
  • [1] THE THERMAL AND METALLURGICAL STATE OF STEEL STRIP DURING HOT-ROLLING .3. MICROSTRUCTURAL EVOLUTION
    DEVADAS, C
    SAMARASEKERA, IV
    HAWBOLT, EB
    [J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1991, 22 (02): : 335 - 349
  • [2] DJAIC RAP, 1972, J IRON STEEL I, V210, P256
  • [3] Dou Xiaofeng, 1998, J UNIV SCI TECHNOL B, V20, P467
  • [4] Ko BC, 1998, MATER SCI TECH SER, V14, P765, DOI 10.1179/026708398790300972
  • [5] RECRYSTALLIZATION OF AUSTENITE AFTER DEFORMATION AT HIGH-TEMPERATURES AND STRAIN RATES - ANALYSIS AND MODELING
    LAASRAOUI, A
    JONAS, JJ
    [J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1991, 22 (01): : 151 - 160
  • [6] KINETICS OF RECOVERY AND RECRYSTALLIZATION IN POLYCRYSTALLINE COPPER
    LUTON, MJ
    PETKOVIC, RA
    JONAS, JJ
    [J]. ACTA METALLURGICA, 1980, 28 (06): : 729 - 743
  • [7] MAVROPOULOS LT, 1988, CAN METALL QUART, V27, P235
  • [8] EFFECT OF ALLOYING ELEMENTS ON METADYNAMIC RECRYSTALLIZATION IN HSLA STEELS
    ROUCOULES, C
    YUE, S
    JONAS, JJ
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1995, 26 (01): : 181 - 190
  • [9] RUIBAL E, 1985, Z METALLKD, V76, P568
  • [10] SELLARS CM, 1990, MATER SCI TECH SER, V6, P1072, DOI 10.1179/026708390790189966