Reduction of NO2 stored in a commercial lean NOx trap at low temperatures

被引:2
作者
Abul-Milh, Miroslawa [1 ]
Westberg, Heije [1 ]
机构
[1] CTP, Volvo Technol Corp, S-41288 Gothenburg, Sweden
关键词
nitrogen oxides; NOx trap; reduction with H-2; reduction with CO; NO2; storage; temperature programmed reduction (TPR); temperature programmed desorption (TPD);
D O I
10.1007/s11244-007-0180-4
中图分类号
O69 [应用化学];
学科分类号
081704 ;
摘要
Isothermal storage of NO2 and subsequent reduction with different reducing agents (H-2, CO or H-2 + CO) in a lean NO (x) trap catalyst was tested by Temperature Programmed Desorption (TPD) and Temperature Programmed Reduction (TPR) experiments at temperatures representative of automotive "cold-start" conditions (< 200 degrees C) using a commercial NO (x) trap catalyst. Results from the TPR experiments revealed that no reduction of stored NO2 to N-2 was observed at 100-180 degrees C, and at 200 degrees C 10% reduction only of NO2 to N-2 was measured. A special affinity of H-2 to form NH3 was observed during the reduction of stored NO2. The formation of NH3 increases with increasing amount of stored NO2 and decreases with increasing storage temperature. Direct relation exists between the amount of adsorbed and/or stored NO2 and the formation of H2O and NH3.
引用
收藏
页码:209 / 214
页数:6
相关论文
共 8 条
[1]   An investigation of the NO/H2/O2 reaction on noble-metal catalysts at low temperatures under lean-burn conditions [J].
Burch, R ;
Coleman, MD .
APPLIED CATALYSIS B-ENVIRONMENTAL, 1999, 23 (2-3) :115-121
[2]   An investigation of promoter effects in the reduction of NO by H2 under lean-burn conditions [J].
Burch, R ;
Coleman, MD .
JOURNAL OF CATALYSIS, 2002, 208 (02) :435-447
[3]  
CODBEN PD, 2000, J MOL CATAL A-CHEM, V158, P115
[4]  
EKFELDT S, 1999, 1990013504 SAE
[5]  
LESAGE T, 2003, CAPOC, V1, P19
[6]   A kinetic study of oxygen adsorption/desorption and NO oxidation over Pt/Al2O3 catalysts [J].
Olsson, L ;
Westerberg, B ;
Persson, H ;
Fridell, E ;
Skoglundh, M ;
Andersson, B .
JOURNAL OF PHYSICAL CHEMISTRY B, 1999, 103 (47) :10433-10439
[7]  
PAZE C, 2003, CAPOC, V2, P215
[8]  
SVEDBERG P, 2003, CAPOC, V2, P238