Effect of Cu excess on three-stage CuGaSe2 thin films using in-situ process controls

被引:16
作者
Caballero, R. [1 ]
Siebentritt, S. [1 ]
Sakurai, K. [1 ]
Kaufmann, C. A. [1 ]
Schock, H. W. [1 ]
Lux-Steiner, M. Ch. [1 ]
机构
[1] Hahn Meitner Inst Berlin GmbH, D-14109 Berlin, Germany
关键词
CuGaSe2; three-stage process; bilayer process;
D O I
10.1016/j.tsf.2006.12.062
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The objective of this work is to study the effect of Cu excess and compare the growth mechanism of CuGaSe2 (CGS) films co-evaporated using a bilayer and a three-stage process and evaluate the consequences of the latter for CGS on transparent back contacts. CGS thin films are prepared by co-evaporation in a three-stage process onto Mo/soda-lime substrates and onto FTO. In contrast to the bilayer process, Cu-Se phases are only observed on the surface at the end of the second stage, e(2). This allows to work with a broader Cu-excess window. Atomic ratios (Cu/Ga)e(2) of around 1.3 at the end of deposition phase 2 in the three-stage process show the better device efficiencies due to a larger grain formation. lncreasing the Cu content leads to a slight decrease of the grain size and voids are observed in the film, reducing the FF of the device. The CGS morphology and the solar cells efficiency are dominated by the Cu excess more than by the T-substrate between 535 degrees C and 500 degrees C. Similar results are obtained for CGS on FTO: (Cu/Ga)e(2) similar to 1.3 as best composition at T-substrate 500 degrees C. (C) 2007 Elsevier B.V. All rights reserved.
引用
收藏
页码:5862 / 5866
页数:5
相关论文
共 12 条
[1]  
ABUSHAMA J, 2005, P 31 IEEE PHOT SPEC
[2]  
CABALLERO R, 2006, P IEEE 4 WORLD C PHO
[3]   Critical issues in the design of polycrystalline, thin-film tandem solar cells [J].
Coutts, TJ ;
Ward, JS ;
Young, DL ;
Emery, KA ;
Gessert, TA ;
Noufi, R .
PROGRESS IN PHOTOVOLTAICS, 2003, 11 (06) :359-375
[4]   Band-gap engineering in Cu(In,Ga)Se-2 thin films grown from (In,Ga)(2)Se-3 precursors [J].
Gabor, AM ;
Tuttle, JR ;
Bode, MH ;
Franz, A ;
Tennant, AL ;
Contreras, MA ;
Noufi, R ;
Jensen, DG ;
Hermann, AM .
SOLAR ENERGY MATERIALS AND SOLAR CELLS, 1996, 41-2 :247-260
[5]   The effect of NaF on Cu(In, Ga)Se2 thin film solar cells [J].
Granath, K ;
Bodegård, M ;
Stolt, L .
SOLAR ENERGY MATERIALS AND SOLAR CELLS, 2000, 60 (03) :279-293
[6]   Transfer of Cu(In,Ga)Se2 thin film solar cells to flexible substrates using an in situ process control [J].
Kaufmann, CA ;
Neisser, A ;
Klenk, R ;
Scheer, R .
THIN SOLID FILMS, 2005, 480 :515-519
[7]  
KLENK R, 1993, ADV MATER, V5, P144
[8]   PREPARATION OF DEVICE-QUALITY CU(IN,GA)SE-2 THIN-FILMS DEPOSITED BY COEVAPORATION WITH COMPOSITION MONITOR [J].
KOHARA, N ;
NEGAMI, T ;
NISHITANI, M ;
WADA, T .
JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1995, 34 (9A) :L1141-L1144
[9]  
Maissel L. I., 1970, HDB THIN FILM TECHNO, P8
[10]   Growth model of CuGaSe2 grains in a Cu-rich/Cu-poor bilayer process [J].
Nishiwaki, S ;
Siebentritt, S ;
Giersig, M ;
Lux-Steiner, MC .
JOURNAL OF APPLIED PHYSICS, 2003, 94 (10) :6864-6870