The activity of non-basal slip systems and dynamic recovery at room temperature in fine-grained AZ31B magnesium alloys

Fine-grained alloys of Mg-3Al-1Zn-0.2Mn in wt.% (AZ31B) were obtained by an equal-channel angular extrusion technique and subsequent annealing at elevated temperatures. Tensile tests were performed at room temperature at a strain rate of 1x10(-3) s(-1). The alloys exhibited an apparent steady-state deformation region and a large tensile elongation of 47%. The deformed microstructure at an elongation of 2% indicated substantial cross-slip to non-basal planes induced by plastic compatibility stress associated with grain boundaries. The non-basal segment of dislocations was found to consist of 40% of the total dislocation density at a yield anisotropy factor of only 1.1 instead of an expected value of 100 obtained from single-crystal experiments. The deformed microstructure at an elongation of 16% indicated recovered regions within twins as well as untwinned matrices. These results indicate that dynamic recovery can occur in Mg alloys at room temperature. (C) 2003 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.