SAXS and the gas transport in polyether-block-polyamide copolymer membranes

被引:109
作者
Barbi, V
Funari, SS
Gehrke, R
Scharnagl, N
Stribeck, N
机构
[1] Univ Hamburg, Inst Tech & Macromol Chem, D-20146 Hamburg, Germany
[2] DESY, HASYLAB, Max Planck Inst Colloids & Interfaces, D-22603 Hamburg, Germany
[3] GKSS Forschungszentrum Geesthacht GmbH, D-21494 Geesthacht, Germany
关键词
D O I
10.1021/ma0213403
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
Membranes from polyether-block-polyamide (PEBA) polymers with varying chemical composition (PEBAX), cast from 1-butanol and cyclohexanol, are studied by small-angle X-ray scattering (SAXS), dry and water-swollen, and as a function of strain. The nanostructure from soft and hard domains is determined. The typical hard domain thickness is 6 nm, and the long period is 17 nm for all grades. Gas transport parameters (permeability, diffusivity, solubility) are determined for He, H-2, CO2, O-2, N-2, and CH4. Increase of polyether domain thickness leads to an increased permeability, but imperfect microphase separation contributes to gas transport properties on the same order of magnitude. Utilizing the interface distribution function (IDF) and the multidimensional chord distribution function (CDF) analysis, we find that the nanostructure of PEBA materials with a high soft block content is hardly changed by variation of casting solvent or water content. Damage of the hard domains occurs during straining. The nanostructure of PEBA materials with a soft block content close to 50% ("balanced") is a function of the casting solvent. Membranes cast from cyclohexanol exhibit a decreased hard domain fraction caused from a declined phase separation. When the hard domains become too small, early failure upon straining is observed. One of the balanced materials exhibits an irregular domain structure; the other two form lamellar stacks with a different degree of order. Swelling in water is controlled by the chemical structure of the blocks. In the PEO/PA6 copolymer both soft and hard phase swell. The swellable PTMeO/ PA12 copolymer shows growth of the soft domains only. Moderate elongation of the materials with a lamellar structure leads to orientation of the hard domain slabs parallel to the direction of strain. The extension of the slabs is < 15 nm. Further elongation induces a microfibrillar structure with increasing heterogeneity. The most probable distance of two neighboring hard domains in the microfibril along the straining direction (long period) remains constant, but the shape of the long period distribution becomes skewed. When domains are destroyed during elongation, there is a tendency to form an orthorhombic macrolattice of almost spherical fragments in addition to the microfibrils.
引用
收藏
页码:749 / 758
页数:10
相关论文
共 39 条
  • [1] Bondar VI, 2000, J POLYM SCI POL PHYS, V38, P2051, DOI 10.1002/1099-0488(20000801)38:15<2051::AID-POLB100>3.0.CO
  • [2] 2-D
  • [3] Bondar VI, 1999, J POLYM SCI POL PHYS, V37, P2463, DOI 10.1002/(SICI)1099-0488(19990901)37:17<2463::AID-POLB18>3.0.CO
  • [4] 2-H
  • [5] BONDAR VI, 1997, P AM CHEM SOC DIV PO, V77, P311
  • [6] Buhmann MD, 2001, ACT NUMERIC, V9, P1, DOI 10.1017/S0962492900000015
  • [7] Bicontinuous-nanostructured polymeric materials from microemulsion polymerization
    Chew, CH
    Li, TD
    Gan, LH
    Quek, CH
    Gan, LM
    [J]. LANGMUIR, 1998, 14 (21) : 6068 - 6076
  • [8] Damian C, 1997, J APPL POLYM SCI, V65, P2579, DOI 10.1002/(SICI)1097-4628(19970919)65:12<2579::AID-APP27>3.3.CO
  • [9] 2-B
  • [10] DENNIS GM, 2000, ACS RUBB DIV M CINC