Deep drawable ultra low carbon Ti IF steels hot rolled in the ferrite region

被引:19
作者
DePaepe, A
Herman, JC
Leroy, V
机构
[1] CRM, Liège
来源
STEEL RESEARCH | 1997年 / 68卷 / 11期
关键词
D O I
10.1002/srin.199701173
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
The control of the amount of solute carbon in ultra low carbon Ti IF steels during ferrite rolling and subsequent recrystallization is of prime importance for the development of an appropriate recrystailization texture End for the production of thin deep drawable hot strips. In the present work, the effect of the solute carbon content and the rolling conditions an the recrystallization texture after ferrite rolling and on the corresponding Lankford value was quantified. Therefore, ultra low carbon Ti if steels with different sulphur and titanium contents were roiled in the ferrite region, in order to obtain a variation in solute carbon content (from 0 to about 10 ppm) at the ferritic rolling temperatures. It was shown that a deep drawing grade (r(mean)> 1.4) can be obtained if the chemical composition of the steel guarantees a complete stabilisation of the solute carbon in the austenitic temperature region and if sufficient strain (85%) is given in the finishing train at temperatures lower than about 800 degrees C. It can be concluded that the sulphur and titanium contents have to be chosen slightly higher in comparison to the conventional Ti IF steel grades used for cold rolling and annealing.
引用
收藏
页码:479 / 486
页数:8
相关论文
共 19 条
  • [1] THERMODYNAMIC CALCULATION OF SOLUTE CARBON AND NITROGEN IN NB AND TI ADDED EXTRA-LOW CARBON-STEELS
    AKAMATSU, S
    HASEBE, M
    SENUMA, T
    MATSUMURA, Y
    AKISUE, O
    [J]. ISIJ INTERNATIONAL, 1994, 34 (01) : 9 - 16
  • [2] BARNETT MR, IN PRESS ISIJ INT
  • [3] HASHIMOTO S, 1990, KOBELCO TECHN REV, P35
  • [4] HERMAN JC, 1994, HOT ROLLING LUBRICAT
  • [5] KESTENS L, 1996, IN PRESS RECRYSTALLI
  • [6] KIM G, 1988, P THERMEC 88 INT C P, P668
  • [7] CALCULATION OF THE TI(CYN1-Y)-TI4C2S2-MNS-AUSTENITE EQUILIBRIUM IN TI-BEARING STEELS
    LIU, WJ
    JONAS, JJ
    [J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1989, 20 (08): : 1361 - 1374
  • [8] EFFECT OF HOT-ROLLING STRAIN-RATE IN THE FERRITE REGION ON THE RECRYSTALLIZATION TEXTURE OF EXTRA-LOW-C SHEET STEELS
    MATSUOKA, S
    SAKATA, K
    SATOH, S
    KATO, T
    [J]. ISIJ INTERNATIONAL, 1994, 34 (01) : 77 - 84
  • [9] MESSIEN P, 1991, REV METALL CIT, P433
  • [10] MEYER L, 1978, THYSSENFORSCH, V2