Effect of water content of ethylene glycol as electrolyte for synthesis of ordered titania nanotubes

Anodization of Ti using fluoride containing polyhydric alcohols such as ethylene glycol or glycerol as electrolyte results in ordered arrays of TiO2 nanotubes with a smooth surface and a very high aspect ratio. However, the reproducibility of the result is affected by many experimental parameters, notably the water content. In this investigation, anodizations of Ti foil in anhydrous ethylene glycol +0.2 wt% NH4F solution (EG solution) with 0-1.0wt% water additions were carried out at 20 V for 45 min in a dry-argon filled controlled-atmosphere glove box. It was observed that a minimum amount of 0.18 wt% of water addition was required to form a well ordered TiO2 nanotubular arrays. When the anhydrous EG solution was reused for third time, ordered arrays of nanotubes started to form. When the water addition to the EG solution was more than 0.5 wt%, formation of ridges was observed on the nanotubes. XPS results showed presence of un-anodized Ti element in the anhydrous condition and presence of organic and (NH4)(2)TiF6 type compounds in all the anodized samples in addition to the regular TiO2 phase. The results underline the influence of water content and local pH condition to form the ordered nanotubular arrays. (c) 2007 Elsevier B.V. All rights reserved.