Slip pattern, microstructure and local crystallography in an aluminium single crystal of copper orientation {112}⟨111⟩

被引:74
作者
Godfrey, A [1 ]
Jensen, DJ [1 ]
Hansen, N [1 ]
机构
[1] Riso Natl Lab, Dept Mat, DK-4000 Roskilde, Denmark
关键词
D O I
10.1016/S1359-6454(97)00316-9
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The evolution of microstructure and local crystallography has been examined in single crystals of {112}[111] orientation of pure Al deformed al room temperature by channel die compression to strains of epsilon = 0.5 and epsilon = 1.5. Despite the channel die deformation mode used, a sample rotation towards the {4 4 11}[11 11 8] orientation was observed. Macroscopic shear bands were not seen. Instead, bands of localised glide on crystallographic planes were observed, associated both with shearing of the microstructure and with + TD rotated orientations. Such strain localisation increased with increasing deformation. The complexity of slip within these regions was confirmed by calculation of dislocation boundary characteristics from local TEM orientation measurements. Dislocation densities calculated using Frank's formula are consistent with the observed macroscopic slip pattern. (C) 1998 Acta Metallurgica Inc.
引用
收藏
页码:835 / 848
页数:14
相关论文
共 31 条
  • [1] OVERVIEW NO-96 - EVOLUTION OF FCC DEFORMATION STRUCTURES IN POLYSLIP
    BAY, B
    HANSEN, N
    HUGHES, DA
    KUHLMANNWILSDORF, D
    [J]. ACTA METALLURGICA ET MATERIALIA, 1992, 40 (02): : 205 - 219
  • [2] DEFORMATION TEXTURE OF CHANNEL-DIE DEFORMED ALUMINUM BICRYSTALS WITH S-ORIENTATIONS
    BLICHARSKI, M
    BECKER, R
    HU, H
    [J]. ACTA METALLURGICA ET MATERIALIA, 1993, 41 (07): : 2007 - 2016
  • [3] LARGE-STRAIN DEFORMATION STRUCTURES IN ALUMINUM CRYSTALS WITH ROLLING TEXTURE ORIENTATIONS
    DRIVER, JH
    JENSEN, DJ
    HANSEN, N
    [J]. ACTA METALLURGICA ET MATERIALIA, 1994, 42 (09): : 3105 - 3114
  • [4] DUGGAN BJ, 1978, METAL SCI
  • [5] Fargette B., 1976, MEMOIRES SCI REV MET, V73-3, P197
  • [6] FORTUNIER R, 1990, YIELDING DAMAGE FAIL, P379
  • [7] SHEAR BANDS IN DEFORMED METALS
    HATHERLY, M
    MALIN, AS
    [J]. SCRIPTA METALLURGICA, 1984, 18 (05): : 449 - 454
  • [8] Hirth J. P., 1992, THEORY DISLOCATIONS
  • [9] HOSFORD W, 1993, MECH CRYSTALS TEXTUR, pCH3