The effect of impactor shape on the impact response of composite laminates

被引：152

作者：

Mitrevski, T ^{[1
]}

Marshall, IH

Thomson, R

Jones, R

Whittingham, B

机构：

[1] Monash Univ, Dept Engn Mech, Clayton, Vic 3800, Australia

[2] Cooperat Res Ctr Adv Composite Struct Ltd, Port Melbourne, Vic 3207, Australia

来源：

COMPOSITE STRUCTURES | 2005年 / 67卷 / 02期

关键词：

carbon/epoxy; impact; impactor shape; low-velocity;

D O I：

10.1016/j.compstruct.2004.09.007

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

The effect of impactor shape on the impact response of thin woven carbon/epoxy laminates is investigated herein. Using a drop weight test rig, specimens were impacted at initial impact energies of 4J and 6J using steel hemispherical, ogival and conical impactors, all 12mm in diameter. The specimens impacted by the conical impactor absorbed most energy as a result of local penetration. The hemispherical impactor produced the highest peak force and lowest contact duration as expected. Only the hemispherical impactor at an initial impact energy of 4J produced barely visible impact damage (BVID) whereas the other impactor shapes produced permanent indentation and penetration. Destructive testing techniques are required to determine the internal damage mechanisms since non-destructive inspection (NDI) techniques provided similar damage areas for the three impactor shapes. (C) 2004 Elsevier Ltd. All rights reserved.

引用

页码：139 / 148

页数：10

共 15 条

[1]

Abrate S., 1991, APPLIED MECHANICS RE, V44, P155, DOI DOI 10.1115/1.3119500

[2]

BAKER AA, 2002, COMPOS PART A-APPL S, V35, P687

[3] RESIDUAL STRENGTH OF A GLASS POLYPROPYLENE COMPOSITE-MATERIAL SUBJECTED TO IMPACT [J].

BENZEGGAGH, ML ;

BENMEDAKHENE, S .

COMPOSITES SCIENCE AND TECHNOLOGY, 1995, 55 (01) :1-11

[4] COMPARISON OF THE LOW AND HIGH-VELOCITY IMPACT RESPONSE OF CFRP [J].

CANTWELL, WJ ;

MORTON, J .

COMPOSITES, 1989, 20 (06) :545-551

[5] RESIDUAL STRENGTH PREDICTION OF IMPACTED CFRP LAMINATES [J].

CAPRINO, G .

JOURNAL OF COMPOSITE MATERIALS, 1984, 18 (06) :508-518

[6] Impact damage and residual strengths of woven fabric glass/polyester laminates [J].

Davies, GAO ;

Hitchings, D ;

Zhou, G .

COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 1996, 27 (12) :1147-1156

[7] THE EFFECT OF STACKING-SEQUENCE ON IMPACT DAMAGE IN A CARBON-FIBER EPOXY COMPOSITE [J].

HITCHEN, SA ;

KEMP, RMJ .

COMPOSITES, 1995, 26 (03) :207-214

[8] Dynamic contact responses of laminated composite plates according to the impactor's shapes [J].

Kim, SJ ;

Goo, NS .

COMPUTERS & STRUCTURES, 1997, 65 (01) :83-90

[9] Experimental and numerical study of the impact behavior of SMC plates [J].

Lee, SM ;

Cheon, JS ;

Im, YT .

COMPOSITE STRUCTURES, 1999, 47 (1-4) :551-561

[10] High velocity perforation behaviour of polymer composite laminates [J].

Mines, RAW ;

Roach, AM ;

Jones, N .

INTERNATIONAL JOURNAL OF IMPACT ENGINEERING, 1999, 22 (06) :561-588

← 1 2 →