Effect of carbon black on properties of rubber nanocomposites

Polymer based nanocomposites were prepared using brominated poly(isobutylene-co-paramethylstyrene) (BIMS) rubber and octadecyl amine modified montmorillonite nanoclay. The effect of nature and loading of carbon black on these nanocomposites and the control BIMS was investigated thoroughly using X-ray diffraction technique (XRD), Fourier transform infrared spectroscopy (FTIR), and mechanical properties. The addition of 4 parts of the modified nanoclay to 20 phr N550 carbon black filled samples increased the tensile strength by 53%. Out of the three different grades of carbon black (N330, N550, and N660), N550 showed the best effect of nanoclay. Optimum results were obtained with the 20 phr filler loading. For comparison, china clay and silica at the same loading were used. Fifty-six and 46% improvements in tensile strength were achieved with 4 parts of nanoclay added to the silica and the china clay filled samples, respectively. N330 carbon black (20 parts) filled styrene butadiene rubber (SBR) based nanocomposite registered 20% higher tensile strength with 4 parts of the modified nanoclay. In all the above carbon black filled nanocomposites, the modulus was improved in the range of 30 to 125%. (C) 2005 Wiley Periodicals, Inc.