Redox behaviour of La-Cr compounds formed in CrOx/La2O3 mixed oxides and CrOx/La2O3/ZrO2 catalysts

被引:20
作者
Hoang, DL
Dittmar, A
Radnik, J
Brzezinka, KW
Witke, K
机构
[1] Inst Appl Chem Berlin Adlershof, D-12489 Berlin, Germany
[2] BAM Fed Inst Mat Res & Testing, D-12489 Berlin, Germany
关键词
chromia containing catalysts; redox reversibility; La-Cr compounds; temperature-programmed reduction; XPS; Raman spectroscopy;
D O I
10.1016/S0926-860X(02)00375-7
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The redox behaviour of chromium oxide in CrOx/La2O3, CrOx/La2O3/ZrO2 and CrOx/ZrO2 mixed oxide systems has been investigated by temperature-programmed reduction (TPR), photoelectron spectroscopy (XPS) and Raman spectroscopy (RS). The formation of La-Cr compounds such as La2CrO6, LaCrO4 was shown to occur by calcination of CrOx/La2O3 and CrOx/La2O3/ZrO2 at 600degreesC. With a Cr content of ca. 4 wt.%, it was revealed that, having been reduced to Cr3+-containing compounds, La2CrO6 and/or LaCrO4 in both systems may be restored by reoxidation at 600degreesC. In the case of CrOx/La2O3/ZrO2 catalysts, it is suggested that these compounds were real surface species anchored as an overlayer on zirconia. Such a structure may stabilise, on the one hand, the tetragonal modification of zirconia and, on the other hand, highly dispersed state of Cr species in calcined as well as in reduced catalysts. (C) 2002 Elsevier Science B.V. All rights reserved.
引用
收藏
页码:95 / 110
页数:16
相关论文
共 38 条
[1]   Control of the textural properties of zirconium oxide [J].
Afanasiev, P ;
Thiollier, A ;
Breysse, M ;
Dubois, JL .
TOPICS IN CATALYSIS, 1999, 8 (3-4) :147-160
[2]   RAMAN-SPECTROSCOPIC STUDIES OF THE POLYMORPHISM IN ZRO2 AT HIGH-PRESSURES [J].
ARASHI, H ;
ISHIGAME, M .
PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE, 1982, 71 (02) :313-321
[3]   SOLID CATALYSTS TREATED WITH ANIONS .21. ZIRCONIA-SUPPORTED CHROMIUM CATALYST FOR DEHYDROCYCLIZATION OF HEXANE TO BENZENE [J].
ARATA, K ;
HINO, M ;
MATSUHASHI, H .
APPLIED CATALYSIS A-GENERAL, 1993, 100 (01) :19-26
[4]  
BERJOAN R, 1973, REV CHIM MINER, V10, P309
[5]   In situ investigation of active sites in zirconia-supported chromium oxide catalysts during the aromatization of n-octane [J].
Brückner, A ;
Radnik, J ;
Hoang, DL ;
Lieske, H .
CATALYSIS LETTERS, 1999, 60 (04) :183-189
[6]  
CHENG W, 1999, J MATER CHEM, V9, P2833
[7]   MoO3/ZrO2 and CrO3/ZrOn catalysts:: Study of the precursor formation [J].
Cimino, A ;
De Rossi, S ;
Dragone, R ;
Ferraris, G ;
Gazzoli, D ;
Valigi, M .
JOURNAL OF COLLOID AND INTERFACE SCIENCE, 1998, 202 (02) :278-292
[8]   XPS quantitative analysis and models of supported oxide catalysts [J].
Cimino, A ;
Gazzoli, D ;
Valigi, M .
JOURNAL OF ELECTRON SPECTROSCOPY AND RELATED PHENOMENA, 1999, 104 (1-3) :1-29
[9]   Methane combustion and CO oxidation on zirconia-supported La, Mn oxides and LaMnO3 perovskite [J].
Cimino, S ;
Colonna, S ;
De Rossi, S ;
Faticanti, M ;
Lisi, L ;
Pettiti, I ;
Porta, P .
JOURNAL OF CATALYSIS, 2002, 205 (02) :309-317
[10]   Structural determination of wear debris generated from sliding wear tests on ceramic coatings using Raman microscopy [J].
Constable, CP ;
Yarwood, J ;
Hovsepian, P ;
Donohue, LA ;
Lewis, DB ;
Munz, WD .
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A, 2000, 18 (04) :1681-1689