Influence of reinforcement weight fraction on microstructure and properties of submicron WC-Cop/Cu bulk MMCs prepared by direct laser sintering

Direct metal laser sintering (DMLS), due to its flexibility in materials and shapes, exhibits a great potential for fabricating complex shaped bulk metal matrix composites (MMCs). In the present work, the submicron WC-10% Co particulate reinforced Cu matrix composites were prepared using DMLS. The influence of reinforcement content on the sintered densification and the attendant microstructures, e.g. the dispersion homogeneity of the reinforcing particulates and the interfacial bonding ability, was investigated using scanning electron microscopy (SEM), energy disperse X-ray (EDX) spectroscopy, and atomic force microscope (AFM). It shows that using a low reinforcement content of 20 wt.% results in a poor densification with severe balling phenomena, due to a higher average composite coefficient of thermal expansion (CTE) and a superheating of the melt. A heterogeneous microstructure with a significant particulate aggregation is obtained at a high reinforcement content of 40 wt.%, because of a limited liquid formation and the resultant high liquid viscosity and reduced Marangoni effect. Using an optimal reinforcement content of 30 wt.% leads to a uniform distribution of the reinforcing particulates and a compatible interfacial microstructure, so as to obtain a favorable sintered density of 90.3% theoretical density. (c) 2006 Elsevier B.V. All rights reserved.