Kinetics of oxidation and decarburization in Al-Si transformation induced plasticity steel

被引:27
作者
Baum, T. L. [1 ]
Fruehan, R. J. [1 ]
Sridhar, S. [1 ]
机构
[1] Carnegie Mellon Univ, Pittsburgh, PA 15213 USA
来源
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE | 2007年 / 38卷 / 02期
基金
美国国家科学基金会;
关键词
D O I
10.1007/s11663-007-9023-8
中图分类号
T [工业技术];
学科分类号
08 [工学];
摘要
This research elucidates the evolution of internal oxidation, external oxidation, and decarburization and their interdependence under different gas atmospheres for a transformation induced plasticity (TRIP) steel sample. A rolled steel sample chemistry of 0.14 wt pct C, 1.8 wt pet Mn, 0.6 wt pet Si, and 1 wt pet Al is used as a case Study. Thermogravimetric techniques are used to examine the net mass change in a sample during isothermal beat treatment under five different atmospheres: P-H2O/P-H2 = 0.01, 0.06, 0.13, 0.20, and 0.32. The results show an initial mass decrease and later an increase. Scanning electron microscopy-energy-dispersive spectroscopy (SEM-EDS), optical microscopy, and glancing-angle X-ray are used to quantify the microstructure and show that the samples have four distinct zones: (1) the external scale, often rich in fayalite; (2) an internally oxidized region with Al, Si, and Mn oxides in an Fe matrix; (3) a decarburized steel region, characterized by large ferrite grains and low carbon content; and (4) a relatively unaffected steel core with a structure similar to the starting material. The results show that the oxidation is predominantly internal and proceeds independently of decarburization, following a parabolic oxidation law where the parabolic rate constant is higher, as would be expected, at higher water vapor contents. Decarburization rates are slightly lower than the predicted rates based on carbon diffusion only, suggesting that the external scale might have an effect in blocking CO escape from the surface.
引用
收藏
页码:287 / 297
页数:11
相关论文
共 24 条
[1]
BIRKS N, 1983, INTRO HIGH TEMPERATU, P151
[2]
DIONNE S, 2004, P INT C ADV LIGHT ST, P405
[3]
Eckert E., 1959, Heat and Mass Transfer
[4]
ELLIOTT JF, 1963, ADISON WESLEY SERIES, P564
[5]
Faral OM, 1999, ISS MWSP CONF P, V37, P253
[6]
Gao J., 2004, P INT C ADV HIGH STR, P107
[7]
Horvath C. D., 2004, GALV 04 C P 6 INT C, P251
[8]
HOSOYA Y, 1997, P NKK CAL FAM M, P148
[9]
HUMPHREYS FJ, 1995, RECRYSTALLIZATION RE, P85
[10]
JONES DA, 1996, PRINCIPLES PREVENTIO, P399