AC impedance spectroscopy study of the corrosion behavior of an AZ91 magnesium alloy in 0.1 M sodium sulfate solution

被引：209

作者：

Chen, Jian ^{[1
]}

Wang, Jianqiu ^{[1
]}

Han, Enhou ^{[1
]}

Dong, Junhua ^{[1
]}

Ke, Wei ^{[1
]}

机构：

[1] Chinese Acad Sci, Inst Met Res, Environm Corros Ctr, Shenyang 110016, Peoples R China

来源：

ELECTROCHIMICA ACTA | 2007年 / 52卷 / 09期

基金：

中国国家自然科学基金;

关键词：

AZ91 magnesium alloy; sodium sulfate; corrosion; EIS; ESEM;

D O I：

10.1016/j.electacta.2006.10.007

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

The corrosion behavior of an AZ91 magnesium alloy in 0.1 M sodium sulfate solution at the corrosion potential (E-corr) was investigated using electrochemical impedance spectroscopy (EIS), environmental scanning electron microscopy (ESEM), energy dispersive X-ray spectroscopy (EDS), and X-ray photoelectron spectroscopy (XPS). The results showed that when the immersion time was less than 18th, general corrosion occurred on the surface and the main corrosion products were hydroxides and sulfates. The film coverage effect was the main mechanism for the corrosion process of AZ91 alloy. At this stage, the matrix had a better corrosion resistance. With the increasing immersion time, pitting occurred on the surface. At this stage, the corrosion process was controlled by three surface state variables: the area fraction theta(1) of the region controlled by the formation of Mg(OH)(2), the area fraction theta(2) of the region controlled by the precipitation of MgAl2(SO4)(4).2H(2)O, and the metastable Mg+ concentration C.. (c) 2006 Elsevier Ltd. All rights reserved.

引用

页码：3299 / 3309

页数：11

共 19 条

[1] Evaluation of microstructural effects on corrosion behaviour of AZ91D magnesium alloy [J].

Ambat, R ;

Aung, NN ;

Zhou, W .

CORROSION SCIENCE, 2000, 42 (08) :1433-1455

[2]

[Anonymous], 1965, CORROS SCI

[3] The corrosion of pure magnesium in aerated and deaerated sodium sulphate solutions [J].

Baril, G ;

Pébère, N .

CORROSION SCIENCE, 2001, 43 (03) :471-484

[4] AC impedance spectroscopy in characterizing time-dependent corrosion of AZ91 and AM50 magnesium alloys -: Characterization with respect to their microstructures [J].

Baril, G ;

Blanc, C ;

Pébère, N .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2001, 148 (12) :B489-B496

[5]

Cao C.N., 2004, CORROSION ELECTROCHE, V2nd

[6] Corrosion behavior of AZ91D magnesium alloy in sodium sulfate solution [J].

Chen, J. ;

Wang, J. ;

Han, E. ;

Dong, J. ;

Ke, W. .

MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2006, 57 (10) :789-793

[7]

Hanawalt JD, 1942, T AM I MIN MET ENG, V147, P273

[8] Atmospheric corrosion of magnesium alloys:: Influence of temperature, relative humidity, and chloride deposition [J].

LeBozec, N ;

Jönsson, M ;

Thierry, D .

CORROSION, 2004, 60 (04) :356-361

[9] THE ROLE OF MG17AL12 PHASE IN THE CORROSION OF MG ALLOY AZ91 [J].

LUNDER, O ;

LEIN, JE ;

AUNE, TK ;

NISANCIOGLU, K .

CORROSION, 1989, 45 (09) :741-748

[10]

MAKAR GL, 1993, INT MATER REV, V38, P138, DOI 10.1179/095066093790326320

← 1 2 →