Syntheses of full-density nanocrystalline titanium nitride compacts by plasma-activated sintering of mechanically reacted powder

被引:40
作者
M. Sherif El-Eskandarany
M. Omori
T. Hirai
T. J. Konno
K. Sumiyama
K. Suzuki
机构
[1] Tohoku University,Department of Chemical Physics of Non Crystalline Materials, Institute for Materials Research
[2] Al-Azhar University,Materials Science and Metallurgy, Mining and Petroleum Engineering Department, Faculty of Engineering
[3] Nasr City,Department of High
[4] Tohoku University,Temperature Materials Science
[5] Tohoku University,Department of Chemical Physics of Non
[6] Tohoku University,Crystalline Materials
[7] Advanced Materials Research,Department of Chemical Physics of Non
关键词
Material Transaction; Select Area Diffraction Pattern; Milled Powder; Consolidate Sample; Iron Contamination;
D O I
10.1007/s11661-998-0023-3
中图分类号
学科分类号
摘要
Nearly equiatomic nanocrystalline titanium nitride (Ti56N44) powder with an average grain size of 5 nm has been synthesized by ball milling elemental Ti powder under nitrogen gas flow at room temperature. During the first stage of reactive ball milling (RBM) (time <3.6 ks), the metallic Ti powder tends to agglomerate to form powder particles with a larger diameter. At the second stage (3.6 to 22.0 ks), the agglomerated particles of Ti fragment to form smaller particles. These smaller particles that have new or fresh surfaces begin to react with the milling atmosphere (nitrogen) during the third stage of milling (22 to 86 ks) to form TiN powder coexisting with unreacted Ti powder. Toward the end of milling (86 to 173 ks), a single phase of nanocrystalline TiN (NaCl structure) is obtained. The powder of this end-product has a spherical-like morphology with an average particle size of about 0.4 μm diameter. A sintering procedure using plasma activation has been employed to consolidate the powder particles at several stages of the RBM. The as-milled and as-consolidated powders have been characterized as a function of the RBM time by means of X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy (SEM), optical metallography, and chemical analyses. Density measurements of the consolidated samples show that after 86 to 173 ks of the RBM time, the compacted samples are essentially fully dense (above 96 pct of the theoretical density for TiN). The results also show that the consolidated TiN compacts still maintain their unique nanocrystalline properties with an average grain size of about 65 nm. The hardness and some mechanical properties of the consolidated TiN compacts have been determined as a function of the RBM time.
引用
收藏
页码:1973 / 1981
页数:8
相关论文
共 57 条
[1]  
Musher J.N.(1996)undefined J. Mater. Res. 11 989-1001
[2]  
Gordon R.G.(1977)undefined Thin Solid Films 40 155-62
[3]  
Nakamura K.(1990)undefined J. Mater. Res. 5 2177-86
[4]  
Inagawa K.(1989)undefined J. Thermal Spraying Soc. Jpn. 26 1150-56
[5]  
Tsuruoka K.(1994)undefined J. Electrochem. Soc. 141 1056-62
[6]  
Komiya S.(1991)undefined Appl. Phys. Lett. 59 1568-70
[7]  
Deevi S.(1992)undefined Mater. Sci. Forum 88–90 801-08
[8]  
Munir Z.A.(1994)undefined J. Mater. Res. 9 2891-98
[9]  
Tsunekawa Y.(1992)undefined Appl. Phys. Lett. 60 1562-63
[10]  
Hirai H.(1994)undefined J. Alloys Compounds 203 117-26