Particle melting behavior during high-velocity oxygen fuel thermal spraying

被引：52

作者：

He J. ^{[1
]}

Ice M. ^{[1
]}

Lavernia E. ^{[1
]}

机构：

[1] Dept. Chem. Biochem. Eng. Mat. Sci., University of California, Irvine, Irvine

来源：

Journal of Thermal Spray Technology | 2001年 / 10卷 / 01期

关键词：

Coatings; Grain size; HVOF; Inconel; 625; Microstructure;

D O I：

10.1361/105996301770349547

中图分类号：

学科分类号：

摘要：

Particle melting behavior during high-velocity oxygen fuel (HVOF) thermal spraying was investigated using Inconel 625 powders. The powder characteristics and coating properties were investigated using scanning electron microscopy (SEM), x-ray, and microhardness studies. Results indicated that the volume fraction of unmelted particles in the coatings was dependent on the proportion of powder within a specified size range, in these experiments, 30 to 50 μm. This particle size range was primarily determined by the particle temperature, which was measured during spraying. Particle temperature significantly decreased as particle size increased. The microhardness values for the coatings containing unmelted particles were predicted by a simple rule-of-mixtures equation for the case of a low volume fraction of unmelted particles. However, for the condition of high volume fraction of unmelted particles, the measured microhardness values did not compare favorably with the calculated values, probably due to the presence of porosity, which occurred in the form of voids found among unmelted particles. The microstructure and characteristics of the feedstock powder were retained in the corresponding coating under certain spray conditions.

引用

页码：83 / 93

页数：10

共 27 条

[1]

Pawlowskia L., The Science and Engineering of Thermal Spray Coatings, (1995)

[2]

Harvery M.D.F., Sturgeon A.J., Blunt F.J., Dunkerton S.B., Thermal Spraying Current Status and Future Trends, pp. 531-535, (1995)

[3]

Varacalle D.J. Jr., Ortiz M.G., Miller C.S., Rotolico A.J., Nerz J., Steeper T.J., Riggs W.L., Thermal Spraying: International Advances in Coatings Technology, pp. 181-187, (1992)

[4]

Knotek O., Schnaut U., Thermal Spray: International Advances in Coatings Technology, pp. 811-816, (1992)

[5]

Eidelman S., Yang X., J. Thermal Spray Technol., 5, pp. 175-184, (1996)

[6]

Eidelman S., Yang X., NanoStructured Mater., 9, pp. 79-84, (1997)

[7]

Sobolev V.V., Guilemany M., Int. Mater. Rev., 41, (1996)

[8]

Guilemany J.M., Llorca-Isern N., Nunez M.D., De Paco J., Scripta Metall. Mater., 31, pp. 1121-1126, (1994)

[9]

Guilemany J.M., Nutting J., Miguel J.R., Dong Z., Scripta Metall. Mater., 33, pp. 55-61, (1995)

[10]

Edris H., Mccartney D.G., Strgeon A.J., J. Mater. Sci., 32, pp. 863-872, (1997)

← 1 2 3 →