QUANTITATIVE HISTOLOGIC EVALUATION OF LTI CARBON, CARBON-COATED ALUMINUM-OXIDE AND UNCOATED ALUMINUM-OXIDE DENTAL IMPLANTS

The response of mandibular bone to identical geometry LTI (Low Temperature Isotropic) carbon, carbon-coated aluminum oxide, and uncoated aluminum oxide blade-type dental implants in baboons for 2 years was evaluated using histologic, microradiographic, and scanning electron microscopic methods. In addition, a quantitative histologic analysis was performed identifying the type, amount, and distribution of tissue surrounding the dental implant systems. This is the final phase of a study investigating the effect of implant elastic modulus and implant surface chemical composition on the performance of dental implants. The results indicate that significant stress shielding of the crestal bone had occurred with the rigid carbon-coated and uncoated aluminum oxide implants when compared to the LTI carbon implants which had a material elastic modulus similar to cortical bone. Based upon the histologic results, it appears that the LTI carbon implants with the direct implant-bone interface exhibited a greater potential for long-term successful performance compared to the aluminum oxide substrate implants.