THE CORROSION BEHAVIOR OF SPUTTER-DEPOSITED AMORPHOUS CR-NI-MO ALLOYS IN 12-M HCL

被引:25
作者
PARK, PY
AKIYAMA, E
HABAZAKI, H
KAWASHIMA, A
ASAMI, K
HASHIMOTO, K
机构
[1] Institute for Materials Research, Tohoku University, Sendai
关键词
D O I
10.1016/0010-938X(94)90188-0
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The synergistic effect of chromium and molybdenum in enhancing the corrosion resistance in the very aggressive acid has been studied by electrochemical measurements and XPS analysis. Amorphous alloys are formed in a wide composition range by the addition of nickel to chromium-molybdenum alloys. The corrosion weight loss decreases with increasing molybdenum content, and Cr-Ni-Mo alloys containing 27 at% or more molybdenum exhibit almost the same corrosion rate as that of molybdenum. Cr-Ni alloys dissolve actively, similarly to chromium, while the molybdenum addition to the Cr-Ni alloys results in spontaneous passivation. The molybdenum addition suppresses the anodic dissolution current because of the formation of tetravalent molybdenum oxyhydroxide having a relatively high activity for both cathodic oxygen and hydrogen reduction with a consequent ennoblement of the open circuit potential. The ennoblement of the open circuit potential leads to the formation of the passive chromium oxyhydroxide film. This film is protective to avoid transpassive dissolution of molybdenum under anodic polarization conditions. The increase in the molybdenum content leads to an increase in the passive current density and to an increase in the unstable Mo6+ content in the film under anodic polarization conditions.
引用
收藏
页码:1395 / 1410
页数:16
相关论文
共 28 条
[1]  
ASAMI K, 1984, CORROS SCI, V24, P83, DOI 10.1016/0010-938X(84)90039-8
[2]   EFFECT OF MOLYBDENUM ON THE ANODIC BEHAVIOR OF AMORPHOUS FE-CR-MO-B ALLOYS IN HYDROCHLORIC-ACID [J].
ASAMI, K ;
NAKA, M ;
HASHIMOTO, K ;
MASUMOTO, T .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1980, 127 (10) :2130-2138
[3]   PRECISELY CONSISTENT ENERGY CALIBRATION METHOD FOR X-RAY PHOTOELECTRON-SPECTROSCOPY [J].
ASAMI, K .
JOURNAL OF ELECTRON SPECTROSCOPY AND RELATED PHENOMENA, 1976, 9 (06) :469-478
[4]   X-RAY PHOTOELECTRON-SPECTRA OF SEVERAL OXIDES OF IRON AND CHROMIUM [J].
ASAMI, K ;
HASHIMOTO, K .
CORROSION SCIENCE, 1977, 17 (07) :559-570
[5]   XPS DETERMINATION OF COMPOSITIONS OF ALLOY SURFACES AND SURFACE OXIDES ON MECHANICALLY POLISHED IRON-CHROMIUM ALLOYS [J].
ASAMI, K ;
HASHIMOTO, K ;
SHIMODAIRA, S .
CORROSION SCIENCE, 1977, 17 (09) :713-723
[6]   SUPERLATTICE-LIKE STRUCTURE OF SPUTTER-DEPOSITED AMORPHOUS ALUMINUM HEAVY ELEMENT ALLOYS [J].
ASAMI, K ;
YOSHIOKA, H ;
HASHIMOTO, K ;
SHIMIZU, K ;
KOBAYASHI, K .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 1989, 110 (2-3) :258-264
[7]   A BIPOLAR MODEL OF THE PASSIVITY OF STAINLESS-STEEL - THE ROLE OF MO ADDITION [J].
CLAYTON, CR ;
LU, YC .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1986, 133 (12) :2465-2473
[8]  
GIESSEN BC, 1982, 4TH P INT C RAP QUEN, V1, P213
[9]   THE EFFECT OF MOLYBDENUM ON THE CORROSION BEHAVIOR OF AMORPHOUS FE-CR-MO-P-C ALLOYS IN HYDROCHLORIC-ACID [J].
HABAZAKI, H ;
KAWASHIMA, A ;
ASAMI, K ;
HASHIMOTO, K .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1991, 134 :1033-1036
[10]  
HABAZAKI H, 1992, CORROS SCI, V33, P425