ELECTRON-MICROSCOPE OBSERVATION OF AUSTENITE AND MARTENSITE IN HIGH ALUMINUM STEEL (SUPPLEMENT)

被引：11

作者：

TADAKI, T ^{[1
]}

SHIMIZU, K ^{[1
]}

机构：

[1] OSAKA UNIV,INST SCI & IND RES,YAMADAKAMI,SUITA 565,OSAKA,JAPAN

来源：

TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS | 1975年 / 16卷 / 02期

关键词：

D O I：

10.2320/matertrans1960.16.105

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

A supplementary examination of the quenched structure of an Fe-9. 70Al-1. 46C steel, after heat treatment not previously used, was carried out by transmission electron microscopy and diffraction, to clarify whether the retained austenite is ordered in the Cu//3Au type, as reported earlier, or is composed of the kappa carbide and the disordered gamma austenite, as suggested by R. Oshima and C. M. Wayman. The new data are interpreted to confirm that the retained austenite is basically ordered in the Cu//3Au type.

引用

页码：105 / 110

页数：6

共 7 条

[1]

LOHBERG K, 1937, ARCH EISENHUTENW, V12, P607

[2] ELECTRON MICROSCOPE OBSERVATION OF MARTENSITE IN HIGH ALUMINIUM STEEL [J].

NISHIYAMA, Z ;

SHIMIZU, KI ;

HARADA, M .

TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1970, 11 (03) :152-+

[3]

NISHIYAMA Z, 1944, J JAPAN I METALS, V8, P305

[4] FINE-STRUCTURE IN QUENCHED FE-AL-C STEELS [J].

OSHIMA, R ;

WAYMAN, CM .

METALLURGICAL TRANSACTIONS, 1972, 3 (08) :2163-&

[5]

Palatnik L.S., 1964, SOV PHYS CRYSTALLOGR, V9, P163

[6] ELECTRON-MICROSCOPIC OBSERVATION OF AUSTENITE AND MARTENSITE IN HIGH ALUMINUM STEEL [J].

TADAKI, T ;

WATANABE, T ;

SHIMIZU, K .

TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1971, 12 (06) :386-&

[7] CRYSTALLOGRAPHY OF MARTENSITE TRANSFORMATION IN FE-AL-C ALLOYS [J].

WATANABE, M ;

WAYMAN, CM .

METALLURGICAL TRANSACTIONS, 1971, 2 (08) :2229-&

← 1 →